Heat capacity of LiInTe2 |
| |
| Authors: | U. C. Boehnke G. Kühn F. I. Frolova I. E. Paukov H. Neumann |
| |
| Affiliation: | (1) Department of Chemistry, Karl Marx University, 7010 Leipzig, Germany;(2) Institute of Inorganic Chemistry, Academy of Science of the USSR, Siberian Branch, 630090 Novosibirsk 90, USSR;(3) Department of Physics, Karl MArx University, 7010 Leipzig, Germany |
| |
| Abstract: | ![]()
The heat capacity of LiInTe2 at constant pressure was measured with an adiabatic vacuum calorimeter in the temperature rangeT=7–300 K. The standard molar enthalpyHm0 —Hm0 (0) and the standard molar entropyS0 (T) were calculated. From a theoretical analysis, the contribution to the heat capacity due to the lattice anharmonicity was estimated.The increased effect of the lattice anharmonicity in LiInTe2 is caused by specific properties of the Li-Te bond.
Zusammenfassung Die Wärmekapazität von LiInTe2 bei konstantem Druck wurde mit einem adiabatischen Vakuumkalorimeter im Temperaturbereich 7  T 300 K bestimmt. Die molare StandardenthalpieHm0 — Hm0 (0) und die molare StandardentropieS0 (T) wurden berechnet. Aus einer theoretischen Analys wurde der Anteil der Gitteranharmonizität an der Wärmekapazität abgeschätzt. Der erhöhte Einfluss der Gitteranharmonitität in LiInTe2 wird durch spezifische Eigenschaften der Li-Te-Bindung verursacht
                            7–300   LiInTe2.    HM0-HM0(0) S0(T).    . LiInTe2   Li- .
|
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
|