Electrochemical activity of nanocrystalline Fe3O4 in aprotic Li and Na salt electrolytes

Fe₃O₄ powders, whose average particle sizes were 400 nm, 100 nm, and 10 nm in diameter, were prepared in order to investigate the effect of particle size on their electrochemical activity. X-ray diffraction and electron microscopy measurements confirmed that all the prepared samples were identified as inverse-spinel type Fe₃O₄, whose crystallite/particle sizes were between 400 nm and 10 nm. We found that the electrochemical activity of Fe₃O₄ in a lithium salt electrolyte was enhanced with a decrease in the particle size from 400 nm to 10 nm. The 10 nm nanocrystalline Fe₃O₄ powder demonstrated the high discharge capacities of about 130 and 160 mAh g⁻¹ with a satisfactory capacity retention as the active cathode material of Li and Na batteries, respectively.