Synthesis, characterization, thermo- and photoluminescence properties of Bi3+ co-doped Gd2O3:Eu3+ nanophosphors

Gd₂O₃:Eu³⁺ (4 mol%) co-doped with Bi³⁺ (Bi = 0, 1, 3, 5, 7, 9 and 11 mol%) ions were synthesized by a low-temperature solution combustion method. The powders were calcined at 800°C and were characterized by powder X-ray diffraction (PXRD), transmission electron microscopy (TEM), Fourier transform infrared and UV–Vis spectroscopy. The PXRD profiles confirm that the calcined products were in monoclinic with little cubic phases. The particle sizes were estimated using Scherrer’s method and Williamson–Hall plots and are found to be in the ranges 40–60 nm and 30–80 nm, respectively. The results are in good agreement with TEM results. The photoluminescence spectra of the synthesized phosphors excited with 230 nm show emission peaks at ～590, 612 and 625 nm, which are due to the transitions ⁵D₀→⁷F₀, ⁵D₀→⁷F₂ and ⁵D₀→⁷F₃ of Eu³⁺, respectively. It is observed that a significant quenching of Eu³⁺ emission was observed under 230 nm excitation when Bi³⁺ was co-doped. On the other hand, upon 350 nm excitation, the luminescent intensity of Eu³⁺ ions was enhanced by incorporation of Bi³⁺ (5 mol%) ions. The introduction of Bi³⁺ ions broadened the excitation band of Eu³⁺ of which a new strong band occurred ranging from 320 to 380 nm. This has been attributed to the 6s²→6s6p transition of Bi³⁺ ions, implying a very efficient energy transfer from Bi³⁺ ions to Eu³⁺ ions. The gamma radiation response of Gd₂O₃:Eu³⁺ exhibited a dosimetrically useful glow peak at 380°C. Using thermoluminescence glow peaks, the trap parameters have been evaluated and discussed. The observed emission characteristics and energy transfer indicate that Gd₂O₃:Eu³⁺, Bi³⁺ phosphors have promising applications in solid-state lighting.