Development of sulphurized SnS thin film solar cells

Thin films of tin sulphide (SnS) have been grown by sulphurization of sputtered tin precursor layers in a closed chamber. The effect of sulphurization temperature (T_s) that varied in the range of 150–450 °C for a fixed sulphurization time of 120 min on SnS film was studied through various characterization techniques. X-ray photoelectron spectroscopy analysis demonstrated the transformation of metallic tin layers into SnS single phase for T_s between 300 °C and 350 °C. The X-ray diffraction measurements indicated that all the grown films had the (111) crystal plane as the preferred orientation and exhibited orthorhombic crystal structure. Raman analysis showed modes at 95 cm^?1, 189 cm^?1 and 218 cm^?1 are related to the A_g mode of SnS. AFM images revealed a granular change in the grain growth with the increase of T_s. The optical energy band gap values were estimated using the transmittance spectra and found to be varied from 1.2 eV to 1.6 eV with T_s. The Hall effect measurements showed that all the films were p-type conducting nature and the layers grown at 350 °C showed a low electrical resistivity of 64 Ω-cm, a net carrier concentration of 2 × 10¹⁶ cm^?3 and mobility of 41 cm² V^?1 s^?1. With the use of sprayed Zn_0.76Mg_0.24O as a buffer layer and the sputtered ZnO:Al as window layer, the SnS based thin film solar cell was developed that showed a conversion efficiency of 2.02%.