Synthesis of well‐defined syndiotactic poly(methyl methacrylate) with low‐temperature atom transfer radical polymerization in fluoroalcohol

The copper‐mediated atom transfer radical polymerization of methyl methacrylate (MMA) in 1,1,1,3,3,3‐hexafluoro‐2‐propanol (HFIP) was studied to simultaneously control the molecular weight and tacticity. The polymerization using tris[2‐(dimethylamino)ethyl]amine (Me₆TREN) as a ligand was performed even at ?78°C with a number‐average molecular weight (M_n) of 13,400 and a polydispersity (weight‐average molecular weight/number‐average molecular weight) of 1.31, although the measured M_n's were much higher than the theoretical ones. The addition of copper(II) bromide (CuBr₂) apparently affected the early stage of the polymerization; that is, the polymerization could proceed in a controlled manner under the condition of [MMA]₀/[methyl α‐bromoisobutyrate]₀/[CuBr]₀/[CuBr₂]₀/[Me₆TREN]₀ = 200/1/1/0.2/1.2 at ?20°C with an MMA/HFIP ratio of 1/4 (v/v). For the field desorption mass spectrum of Cu^IBr/Me₆TREN in HFIP, there were [Cu(Me₆TREN)Br]⁺ and [Cu(Me₆TREN)OCH(CF₃)₂]⁺, indicating that HFIP should coordinate to the Cu^I/Me₆TREN complex. The syndiotacticity of the obtained poly(methyl methacrylate)s increased with the decreasing polymerization temperature; the racemo content was 84% for ?78°C, 77% for ?30°C, 75% for ?20°C, and 63% for 30°C. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 1436–1446, 2006