本文比较了由化学气相沉积法制备的不同直径(在100 nm以内)的多壁碳纳米管(CNT)的抗电化学氧化性.将CNT电极于1.2 V(vs.RHE)下电氧化120 h,记录氧化电流~时间变化曲线;X射线光电子能谱(XPS)分析氧化前后CNT的表面化学组成.结果表明,随着CNT直径的减小,其氧化电流降低,但其中以为10~20 nm的CNT电极氧化电流最小,表面氧的增量也最小,即被氧化的程度最低,抗电化学氧化性最强.根据不同直径CNT的缺陷位、不定型碳的丰度和碳原子的应力能,分析了其抗电化学氧化性差异的原因.

Investigation on the Resistance to Electrochemical Oxidation of Carbon Nanotubes with Various Diameters

The resistance to electrochemical oxidation of multi-wall carbon nanotubes(CNT) with various diameters is investigated by applying a fixed potential of 1.2 V(RHE) for 120 h in 0.5 mol L~(-1) H_(2)SO_(4).The oxidation current of CNTs decreases with their diameters,but CNTs between 10~20 nm in diameter(D1020) shows the lowest oxidation current.XPS analysis shows that,after oxidation,the increase in surface oxygen for D1020 is the smallest,implying that the oxidation degree for D1020 is the lowest.The conclusion can be reached that CNTs between 10~20 nm in diameter are the most resistant to electrochemical oxidation.The difference in electrochemical stability of CNTs is attributed to the difference in CNT structure: the amount of defects and amorphous carbon and the carbon atom strain caused by the curvature.