Optical characterization of InGaN/AlGaN/GaN diode grown on silicon carbide

Electroluminescence (EL) properties of In_xGa_1−xN/Al_yGa_1−yN/GaN/SiC diode were studied. The spectral range for which EL spectra were recorded is 1–3.5 eV. Room temperature EL was obtained for forward bias (3.18 V, 220 μA) at 446.067 nm (blue luminescence band), 606.98 nm (yellow luminescence band) and 893.84 nm (Infrared luminescence band). The EL temperature dependence shows that, BL band is mostly given by e–h recombination corresponding to indium composition equal to 0.17 ± 0.01 and 0.14 ± 0.02 obtained theoretically and experimentally, respectively. The yellow band is generally weak and absent at low temperature. The IRL band is more consistent with the DAP recombination and could be explained by the thermal activation of Mg states. The luminescence bands shift to lower energies is due probably to the larger potential fluctuations effect.