Intense Upconversion Luminescence of Yb3+-Er3+ in Li2O Content Tungsten-tellurite Glasses

The Er³⁺ -Yb³⁺ codoped in Li₂O content tungsten -tellurite (TWL) transparent glasses are synthesized and measured the absorption, Raman and upconversion luminescence (UPL) spectra. At room temperature intense green emission peak at 560 nm ( ⁴S_3/2→⁴I_15/2) and red emission peak at 670 nm ( ⁴F_9/2→⁴I_15/2) of Er³⁺ observed even at minimum 86 mW pumping power of infrared 980 nm excitation. For structure of the TWL glass, Raman spectrum result revealed that an important role of WO₃ in the formation of glass network linkage with Li₂O. Under this influence estimated lifetime of the ⁴I_11/2 of Er³⁺ was 1.89 μs and due to lower phonon energy of the glass produce strong upconversion signal. The effect of Er₂O₃ concentration on emission intensity result indicated that green emission intensity initially increase in compare to red emission. Under the 980 nm pump power variation measured the relatively increases the red emission to the green emission intensity and analyze the possible upconversion mechanism and process.