Thermal analysis of the double-melting behavior of poly(L-lactic acid)

The melting and crystallization behavior of poly(L -lactic acid) (PLLA; weight-average molecular weight = 3 × 10⁵) was studied with differential scanning calorimetry (DSC). DSC curves for PLLA samples were obtained at various cooling rates (CRs) from the melt (210 °C). The peak crystallization temperature and the exothermic heat of crystallization determined from the DSC curve decreased almost linearly with increasing log(CR). DSC melting curves for the melt-crystallized samples were obtained at various heating rates (HRs). The double-melting behavior was confirmed by the double endothermic peaks, a high-temperature peak (H) and a low-temperature peak (L), that appeared in the DSC curves at slow HRs for the samples prepared with a slow CR. Peak L increased with increasing HR, whereas peak H decreased. The peak melting temperatures of L and H [T_m(L) and T_m(H)] decreased linearly with log(HR). The appearance region of the double-melting peaks (L and H) was illustrated in a CR–HR map. Peak L decreased with increasing CR, whereas peak H increased. T_m(L) and T_m(H) decreased almost linearly with log(CR). The characteristics of the crystallization and double-melting behavior were explained by the slow rates of crystallization and recrystallization, respectively. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 25–32, 2004