Investigation of surface structure and composition of in situ annealed Fe–Mn binary alloy samples using RHEED and electron spectroscopy |
| |
Authors: | C Martínez R Cremer D Neuschütz J P Servais D Loison |
| |
Institution: | 1. Lehrstuhl für Theoretische Hüttenkunde, RWTH Aachen, Kopernikusstraße 16, 52056 Aachen, Germany;2. CRM, Rue Solvay 11, Liège, Belgium;3. IRSID, Voie Romaine, BP 30320, 57283 Maizières-Les-Metz, France |
| |
Abstract: | The formation of oxides at the surface of Fe–1.5%Mn and Fe–0.6%Mn binary alloys was investigated as a function of the conditions of the heat treatments. Both the influence of temperature and the atmosphere under which the experiments were performed were studied. The range of annealing temperatures was adjusted to 800°C. The atmosphere consisted of a mixture of N2–5%H2 and traces of water vapour, with different fixed dew points ranging from ?10°C to ?30°C. The state of the annealed surfaces was determined using in situ analytical devices attached to the annealing reactor in order to avoid surface contamination or the formation of native oxides after the experiments due to contact with air. The structure and composition of the surfaces were determined by reflection high-energy electron diffraction (RHEED) and electron spectroscopy (XPS, AES). Copyright © 2002 John Wiley & Sons, Ltd. |
| |
Keywords: | selective oxidation Fe–Mn alloys in situ annealing XPS RHEED |
|
|