Flux pinning in columnar-structured and single crystalline MgB2 films

We have investigated the flux pinning effect of columnar grain boundary in columnar-structured and single crystalline MgB₂ films. The MgB₂ films with columnar structure showed much higher J_c than that of single crystalline thin film, and sample having smaller grain size had a higher J_c in high magnetic fields. At 5 K, the MgB₂ film with grain size of 460 nm showed an abnormal double-peak behavior in pining force density, F_p(B), caused by competition of different types of pinning sites, such as planar defects and point defects. Field dependences of F_p in columnar-structured films suggest that the columnar grain boundary is a strong pinning source in the MgB₂ film and it plays a crucial role in enhancing J_c over a wide range of magnetic fields and temperatures.