Crystallization kinetics of chalcogenide glass Se0.8 Te0.2 |
| |
| Authors: | M M Hafiz N Afify M A Osman M Dongol |
| |
| Institution: | (1) Phys. Deft., Assiut Univ., Egypt;(2) Phys. Dept., Fac. of Sci. (Qena), Assiut Univ., Egypt |
| |
| Abstract: | The crystallization kinetics of the chalcogenide glass Se0.8Te0.2 was studied by means of differential scanning calorimetry. The variation in partial area (X) with temperature (T) revealed that the transition from the amorphous to the crystalline phase occurs in two dimensions.Activation energies were determined for both the glass transition (E
t) and the crystallization (E
c).E
t was calculated from the variation inT
g with the heating rate (a).E
c was determined by three different methods: (i) variation inX withT, (ii) variation inT
p
witha, and (iii) variation inT
c witha.E
t andE
c have values of 161.01±2.75 and 84.75 ±8.21 kJ/mol, respectively.
Zusammenfassung Mittels DSC wurde die Kristallisierungskinetik des Chalkogenidglases Se0.8Te0.2 untersucht. Eine Änderung partieller Gebiete (X) mit der Temperatur (T) zeigte, daß der Übergang von der amorphen zur kristallinen Phase zweidimensional verläuft.Es wurde die Aktivierungsenergie sowohl für den Glasübergang (E
t) als auch für die Kristallisierung (E
c) bestimmt.E
t wurde mittels der Abhängigkeit vonT
g von der Aufheizgeschwindigkeit (a) ermittelt.E
c wurde auf drei verschiedene Wege bestimmt: (i) Änderung vonX in Abhängigkeit vonT, (ii) Änderung vonT
p in Abhängigkeit vona und (iii) Änderung vonT
c in Abhängigkeit vona. Die Werte vonE
t undE
c betragen 161.01±2.75 bzw. 84.75±8.21 kJ/mol.