| Abstract: | Aqueous acrylic‐polyurethane (AC–PU) hybrid emulsions were prepared by semibatch emulsion polymerization of methyl methacrylate (MMA) in the presence of four polyurethane (PU) dispersions. The PU dispersions were synthesized with isophorone diisocyanate (IPDI), 1000 and 2000 molecular weight (MW) poly(neopentyl) adipate, 1000 MW polytetramethyleneetherglycol, butanediol (BD), and dimethylol propionic acid (DMPA). MMA was added in the monomer emulsion feed. We studied the effect of the use of different PU seed particles on the rate of polymerization, the particle size and distribution, the number of particles, and the average number of radicals per particle. The PU rigidity was controlled by varying the polyol chemical structure, the polyol MW (Mn), and by adding BD. The monomer feed rate was varied to study its influence on the process. It was observed that the PU particles that had been prepared with a higher MW polyol swelled better with MMA before the monomer‐starved conditions occurred. There seemed to be no significant discrepancies between the series with different PU seeds in the monomer‐starved conditions. The overall conversion depended on the monomer addition rate, and the polymerization rate acquired a constant value that was comparable to the value of the monomer addition rate. The instantaneous conversion increased slightly. The average particle size increased, and the total particle number in the reactor was constant and similar to the number of PU particles in the initial charge. The average number of radicals per particle increased. The differences between the system with a constant particle number and average number of radicals per particle and the system with a fixed radical concentration are discussed. The semibatch emulsion polymerization of MMA in the presence of PU particles studied was better compared to the system with a fixed radical concentration. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 844–858, 2005 |