Preparation and properties of crosslinked hybrid proton exchange membrane based on sulfonated poly (arylene ether nitrile) with improved selectivity for fuel cell application

Novel sulfonated poly (arylene ether nitrile) with pendant carboxylic group copolymers have been prepared as proton exchange membranes which were applied in direct methanol fuel cells (DMFCs). Compared with others, this work shows two main advantages: the crosslinked method is uncomplicated and the membranes were prepared via the hydroquinonesulfonic acid potassium salt (SHQ) as crosslinker mingled in sulfonated poly (arylene ether nitrile) (SPEN) to avoid the decrease of proton conductivity. The obtained crosslinked membranes exhibited improved dimensional stability; larger tensile strength than that of pure SPEN; and good thermal, mechanical properties. Furthermore, after crosslinking, the membranes had low methanol permeability values (0.78–3.4 × 10^?7 cm² s^?1) and displayed good proton conductivities in the range of 0.0328–0.0385 S·cm^?1 at room temperature. The sample of SPEN-SHQ-5 % showed highest selectivity value of 4.205 × 10⁵ S·s cm^?3, which was 11.9 times higher than that of Nafion 117. All of these results indicated that these membranes would be the potential candidates as proton exchange membranes (PEMs) in DMFCs.