La2Si2O7 im I—Typ: Gemäß La6[Si4O13][SiO4]2 kein echtes Lanthandisilicat

I‐Type La₂Si₂O₇: According to La₆[Si₄O₁₃][SiO₄]₂ not a Real Lanthanum Disilicate In attempts to synthesize lanthanum telluride silicate La₂Te[SiO₄] (from La, TeO₂, SiO₂ and CsCl, molar ratio: 1 : 1: 1 : 20, 950 °C, 7 d) or fluoride‐rich lanthanum fluoride silicates (from LaF₃, La₂O₃, SiO₂ and CsCl, molar ratio: 5 : 2 : 3 : 17, 700 °C, 7 d) in evacuated silica tubes, colourless lath‐shaped single crystals of hitherto unknown I‐type La₂Si₂O₇ (monoclinic, P2₁/c; a = 726.14(5), b = 2353.2(2), c = 1013.11(8) pm, β = 90.159(7)°) were found in the CsCl‐flux melts. Nevertheless, this new modification of lanthanum disilicate does not contain any discrete disilicate groups [Si₂O₇]^6‐ but formally three of them are dismutated into one catena‐tetrasilicate ([Si₄O₁₃]^10‐ unit of four vertex‐linked [SiO₄]^4‐ tetrahedra) and two ortho‐silicate anions (isolated [SiO₄]^4‐ tetrahedra) according to La₆[Si₄O₁₃][SiO₄]₂. This compound can be described as built up of alternating layers of these [SiO₄]^4‐ and the horseshoe‐shaped [Si₄O₁₃]^10‐ anions along [010]. Between and within the layers the high‐coordinated La ³⁺ cations (CN = 9 ‐ 11) are localized. The close structural relationship to the borosilicates M₃[BSiO₆][SiO₄](M = Ce ‐ Eu) is discussed and structural comparisons with other catena‐tetrasilicates are presented.