Layered Double Hydroxides MgFe-LDH and MgAl-LDH have been prepared by the method involving separate nucleation and ageing steps. The structure analyses for these two materials show that the values of the parameters both a and c of MgAl-LDH are smaller than that of MgFe-LDH though their structures are similar, and MgAl-LDH with higher crystallinity is more easily formed than MgFe-LDH in the same preparing conditions. The IR analyses manifest that the structures of layer sheets and the orderings of the anions in the interlayer regions of MgAl-LDH are more regular than that of MgFe-LDH. The temperature programmed XRD analyses reveal that the diffraction peak of 003 reflections for MgAl-LDH could be seen after calcining at 300℃, while this peak for MgFe-LDH disappears after calcining at 200℃. Together with the TG-DTA analysis it can be concluded that the thermal stability of MgAl-LDH is obviously higher than that of MgFe-LDH.

Studies on Structures and Properties of MgAl and MgFe Layered Double Hydroxides