Electronic properties of the polycrystalline tin dioxide interface with conjugated organic layers

The results on the electronic structure of the unoccupied electronic states of the polycrystalline SnO₂ in the energy range from 5 eV to 25 eV above the Fermi level are presented. The modification of the electronic structure and of the surface potential upon deposition of the ultrathin films of copper phthalocyanine (CuPc) and of perylene tetracarboxylic acid dianhydride (PTCDA) film onto the SnO₂ surface were studied using the very low energy electron diffraction (VLEED) method and the total current spectroscopy (TCS) measurement scheme. A substantial attenuation of the TCS signal coming from the SnO₂ surface was observed upon formation of a 1.5–2 nm thick organic deposit layer while no new spectral features from the deposit were distinguishable. It was observed that the electronic structure typical for the organic films was formed within the organic deposit thickness range from 2 nm to 7 nm. The interfacial charge transfer was characterized by the formation of the polarization layer up to 5 nm thick in the organic films. The PTCDA deposition on SnO₂ was accompanied by the negative charge transfer onto the organic layer and to the 0.65 eV increase the surface work function. At the CuPc/SnO₂ interface, the negative charge was transferred to the SnO₂ surface and the overall surface work function decreased by 0.15 eV.