SYNTHESIS AND CHARACTERISTICS OF POLY(ARYLENE ETHER DIKETONE)S

Poly(arylene ether diketone)s were prepared by the aromatic nucleophilicdisplacement reaction of 4,4'-difluorobenzil with different bisphenols in the presence of an-hydrous potassium carbonate in diphenylsulfone at elevated temperature. The polymersobtained had inherent viscosity of 0.51 ～ 0.63 dL/g, and exhibited glass transition temper-ature ranging from 136 ～217℃ mainly depending on the bisphenols used in the polymersynthesis. Thermogravimetry of these polymers showed excellent thermal stability, indi-cating that 10% weight losses of the polymers were observed in the range above 428℃ and438℃ in air and nitrogen, respectively. The mechanical properties of these polymers werealso described and the permeability of five polymers for H_2, O_2 and N_2 was determined at30℃.

SYNTHESIS AND CHARACTERISTICS OF POLY (ARYLENE ETHER DIKETONE)S

 Poly(arylene ether diketone)s were prepared by the aromatic nucleophilicdisplacement reaction of 4,4'-difluorobenzil with different bisphenols in the presence of an-hydrous potassium carbonate in diphenylsulfone at elevated temperature. The polymersobtained had inherent viscosity of 0.51 ～ 0.63 dL/g, and exhibited glass transition temper-ature ranging from 136 ～217℃ mainly depending on the bisphenols used in the polymersynthesis. Thermogravimetry of these polymers showed excellent thermal stability, indi-cating that 10% weight losses of the polymers were observed in the range above 428℃ and 438℃ in air and nitrogen,respectively.The mechanical properties of these polymers were also described and the permeability of five polymers for H₂,O₂and N₂ was determined at 30℃.