Luminescence centers in thin films of yttrium oxide and yttrium-aluminum garnet activated with bismuth

Luminescence spectra and photoluminescence excitation spectra of Y₂O₃:Bi and Y₃Al₅O₁₂:Bi thin films were investigated. Luminescence was stimulated by the emission from two types of centers that were associated with the substitution of Bi³⁺ for Y³⁺ in sites of the crystal lattice of Y₂O₃ (Y₃Al₅O₁₂) with point symmetries C₂ and C_3i (D₂ and C_3i). The emission of Bi³⁺ in the site with point symmetry C_3i causes blue luminescence in both Y₂O₃:Bi and Y₃Al₅O₁₂:Bi films with maxima at 3.03 eV and 3.15 eV, respectively, that is related to the ³P₁-¹S₀ transition. The emission of Bi³⁺ in the site with point symmetry C₂ gives green luminescence in Y₂O₃:Bi with the maximum at 2.40 eV that is also related to the ³P₁-¹S₀ transition. The emission of Bi³⁺ in the site with point symmetry D₂ leads to ultraviolet luminescence in Y₃Al₅O₁₂:Bi with the maximum at 3.75 eV that corresponds to the ³P₁-¹S₀ transition. The red luminescence band with the maximum at 1.85 eV in Y₂O₃:Bi is due to the presence of structural defects. __________ Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 75, No. 2, pp. 202–207, March–April, 2008.