Enhancement of the emission from TeO2 nanorods by encapsulation with ZnO

TeO₂‐core/ZnO‐shell nanorods were synthesized by a two–step process comprising thermal evaporation of Te powders and atomic layer deposition of ZnO. Scanning electron microscopy images exhibit that the core‐shell nanorods are 50 ‐ 150 nm in diameter and up to a few tens of micrometers in length, respectively. Transmission electron microscopy and X‐ray diffraction analysis revealed that the cores and shells of the core‐shell nanorods were polycrystalline simple tetragonal TeO₂ and amorphous ZnO with ZnO nanocrystallites locally, respectively. Photoluminescence measurement revealed that the TeO₂ nanorods had a weak broad violet band at approximately 430 nm. The emission band was shifted to a yellowish green region (∼540 nm) by encapsulation of the nanorods with a ZnO thin film and the yellowish green emission from the TeO₂‐core/ZnO‐shell nanorods was enhanced significantly in intensity by increasing the shell layer thickness. The highest emission was obtained for 125 ALD cycles (ZnO coating layer thickness: ∼15 nm) and its intensity was much higher than that of the emission from the uncapsulated TeO₂ nanorods. The origin of the enhancement of the emission by the encapsulation is discussed in detail. (© 2011 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)