Mixed perovskite oxides with CaxLa1-xNi0.3Al0.7O3-d and SrxLa1-xNi0.3Al0.7O3-d(x=0,0.2,0.5,0.8,and 1.0;d=0.5x)components have been prepared by a sol-gel method.The effects of the partial substitution of La by Ca and Sr in dry CH4 reforming were investigated at 500-800 ℃ and 101 kPa.The resulting oxides were examined by Fourier-transform infrared spectroscopy,X-ray diffraction,temperature-programmed reduction,scanning electron microscopy,energy dispersive X-ray spectrometry,and BET surface area analysis.Studies following the catalytic tests by carbon analysis show some carbon deposition on this catalytic system.The results indicate that all initial salt entered into a propionate structure,and that most of the solid solution has well defined perovskite structure with surface areas between 3.5 and 9.5 m2/g.Most of the catalysts performed well in the dry reforming,with CH4 conversions up to 90%,H2 yields up to 80%,and H2 selectivity up to 90%.Among the samples,Sr0.2La0.8Ni0.3Al0.7O2.9 showed an excellent catalytic performance in CH4 dry reforming,with a H2/CO ratio of 1,whereas Ca0.8La0.2Ni0.3Al0.7O2.6 showed the lowest coke formation(approximately 0.71%).

Effects of Lanthanum Substitution by Strontium and Calcium in La-Ni-Al Perovskite Oxides in Dry Reforming of Methane

Mixed perovskite oxides with CaxLa1-xNi0.3Al0.7O3-d and SrxLa1-xNi0.3Al0.7O3-d(x=0,0.2,0.5,0.8,and 1.0;d=0.5x)components have been prepared by a sol-gel method.The effects of the partial substitution of La by Ca and Sr in dry CH4 reforming were investigated at 500-800℃ and 101 kPa.The resulting oxides were examined by Fourier-transform infrared spectroscopy,X-ray diffraction,temperature-programmed reduction,scanning electron microscopy,energy dispersive X-ray spectrometry,and BET surface area analysis.Studies following the catalytic tests by carbon analysis show some carbon deposition on this catalytic system.The results indicate that all initial salt entered into a propionate structure,and that most of the solid solution has well defined perovskite structure with surface areas between 3.5 and 9.5 m2/g.Most of the catalysts performed well in the dry re-forming,with CH4 conversions up to 90%,H2 yields up to 80%,and H2 selectivity up to 90%.Among the samples,Sr0.2La0.8Ni0.3Al0.7O2.9 showed an excellent catalytic performance in CH4 dry reforming,with a H2/CO ratio of 1,whereas Ca0.8La0.2Ni0.3Al0.7O2.6 showed the lowest coke formation(approximately 0.71%).