A fluorene diol derivative, 9,9‐bis[4‐(2‐hydroxyethoxy)phenyl]fluorene ( 1 ), reacted with diisocyanates such as 1,3‐bis(isocyanatomethyl)cyclohexane ( 2a ), 1,6‐diisocyanatohexane ( 2b ), and 1,3‐bis(isocyanatomethyl)benzene ( 2c ) under temperature‐controlled microwave irradiation to form the corresponding polyurethanes with being 30 000 to 60 000, measured by GPC with reference to polystyrene standards within 5 to 10 min at 160 to 200 °C. In the reactions of 2a and b , the molecular weights were 15 to 20 times higher than those obtained by conventional oil bath heating. For a solvent of the microwave‐promoted reaction, a hydrocarbon compound, decalin, is preferably used to undergo the polymerization cleanly without unfavorable coloration and/or gelation.
being 30 000 to 60 000, measured by GPC with reference to polystyrene standards within 5 to 10 min at 160 to 200 °C. In the reactions of 2a and b , the molecular weights were 15 to 20 times higher than those obtained by conventional oil bath heating. For a solvent of the microwave‐promoted reaction, a hydrocarbon compound, decalin, is preferably used to undergo the polymerization cleanly without unfavorable coloration and/or gelation. 