Thermal stability of poly(β-bromostyrene) and copolymers of β-bromostyrene with methyl methacrylate |
| |
| Authors: | A A El-Agamey M A Diab |
| |
| Institution: | (1) Chemistry Department, Faculty of Education, Mansoura University, Demiatta, Egypt |
| |
| Abstract: | The thermal stabilities of poly( -bromostyrene), poly-(methyl methacrylate) homopolymers and copolymers of-bromostyrene-methyl methacrylate covering the entire composition range were studied using TG analysis. At each extreme of the composition range, incorporation of comonomer units results in a copolymer more stable than the brominated homopolymer. Maximum stability occurs for compositions of approximately 62 mole percent-bromostyrene. The formation of the anhydride structure among the degradation products leads to the stability of the copolymers.
Zusammenfassung Die thermische Stabilität von-Bromstyrol- und Methylmethacrylat-Homopolymeren sowie von sich über den ganzen Zusammensetzungsbereich erstreckenden-Bromstyrol/Methylmethacrylat-Kopolymeren wurde thermogravimetrisch untersucht. An beiden Enden des Zusammensetzungsbereichs führt der Einbau von Komonomereinheiten zu einem Kopolymer, das stabiler als das bromierte Homopolymer ist. Maximale Stabilität wird bei einem Gehalt von etwa 62 Mol-%-Bromstyrol erreicht. Die Bildung der Anhydridstruktur führt zur Stabilität des Kopolymers.
                       /- ,  -  .      ,   . - 62%.  .
Presented at the World Conference of Thermal Analysis, held in Bad Hofgastein (Austria), 1985. |
| |