| Abstract: | A novel hyperbranched polyester acrylate (HPEA) was synthesized based upon ethylenediamine tetraacetic acid as a “core” molecule, 5‐hydroxyisophthalic acid as an AB2 monomer, and 2‐hydroxyethyl acrylate as an endcapping reagent. The obtained oligomer has an unsaturation concentration of 4.10 mmolC?C g?1 measured by nuclear magnetic resonance and a wide molecular weight distribution of 1.64 measured by gel permeation chromatography. The two‐photon absorption (TPA) photopolymerization of HPEA under the exposure of a Ti : sapphire femtosecond laser with a wavelength of 800 nm was investigated through laser exposure dose‐dependant spatial resolutions of its resins. The TPA photopolymerization thresholds at the range 1.6–4.3 × 107 mJ cm?2, and exposure dose windows at the range 3.4–4.3 for three formulations were determined. A spatial resolution of 0.85 μm was obtained through the TPA photopolymerization of the formulation containing 1 wt% photoinitiator and 0.3 wt% photoinhibitor. A diffraction grating and real three‐dimensional coupled gear wheel created by TPA photopolymerization were described to demonstrate the unique capability of HPEA in microfabrications. Copyright © 2004 John Wiley & Sons, Ltd. |