Preparation and Characterization of Highly Proton-Conductive Composites Composed of Phosphoric Acid-Doped Silica Gel and Styrene-Ethylene-Butylene-Styrene Elastomer

Highly proton-conductive elastic composites have been successfully prepared from H₃PO₄-doped silica gel and a styrene-ethylene-butylene-styrene (SEBS) block elastic copolymer. Ionic conductivities of the composites depended on the concentration of H₃PO₄ and the heat treatment temperature of the H₃PO₄-doped silica gel. It was found that H₃PO₄ added is present mainly as free orthophosphoric acid in the silica gel. The composite composed of H₃PO₄-doped silica gel with a molar ratio of H₃PO₄/SiO₂ = 0.5 heat-treated at temperatures below 200°C and SEBS elastomer in 5 mass% showed a high conductivity of 10^–5 S cm^–1 at 25°C in an dry N₂ atmosphere. The water adsorption during a storage in 25% relative humidity at room temperature for 1 day enhanced the ionic conductivities of composites by about one order of magnitude. Lower conductivities obtained in the composite with the H₃PO₄-doped silica gel heat-treated at 250°C for 1 h were due to the formation of crystalline Si₃(PO₄)₄. The temperature dependence of conductivity of the composites was the Vogel-Tamman-Fulcher type, indicating that proton was transferred through a liquidlike phase formed in micropores of the H₃PO₄-doped silica gels. The temperature dependence of the modulus of the composite was similar to that of the SEBS elastomer. The thermoplastically deforming temperature of the composite was around 100°C, which was higher by 30°C than that of the SEBS elastomer.