Effect of zeolite pore morphology on solvent-less alkylation of benzene with 1-hexene

In an attempt to convert the carcinogenic benzene which is almost restricted for its use in gasoline, alkylation reaction with olefin 1-hexene has been conducted on various zeolites. Four zeolites having different pore topology and pore size have been applied as solid acid catalysts for effective production of alkylate in a liquid phase, solvent-less low temperature reaction. The textural properties of all the four zeolites (ZSM-5, MOR, BEA, HY) have been characterized for crystal morphology by TEM, crystal structure by XRD and FTIR, BET for surface area, N₂ sorption for porosity and TPD for acidity. Among the zeolite, BEA possessed high surface area (600.61 m²/g) and enhanced meso pores volume (0.3956 cm³/g) as compared to other zeolite samples. The performance of BEA was also observed to be superior in the liquid phase alkylation of benzene with 1-hexene in a batch reactor under autogenous pressure without using any solvent. At the optimum reaction conditions, the benzene conversion was 86.6 wt% and 3-Phenylhexane, 2-Phenylhexane yield were about 47.9 wt% and 38.7 wt% respectively on this catalyst. The BEA also exhibited longer time-on-stream and reusability performance, thus offers an attractive route for converting benzene into valuable (3-Phenylhexane, 2-Phenylhexane) alkylate product useful for the manufacturing of fine chemicals, dyestuff, detergents and scents.