Sono-assisted preparation of highly-efficient peroxidase-like Fe3O4 magnetic nanoparticles for catalytic removal of organic pollutants with H2O2

Fe₃O₄ magnetic nanoparticles (Fe₃O₄ MNPs) with much improved peroxidase-like activity were successfully prepared through an advanced reverse co-precipitation method under the assistance of ultrasound irradiation. The characterizations with XRD, BET and SEM indicated that the ultrasound irradiation in the preparation induced the production of Fe₃O₄ MNPs possessing smaller particle sizes (16.5 nm), greater BET surface area (82.5 m² g^?1) and much higher dispersibility in water. The particle sizes, BET surface area, chemical composition and then catalytic property of the Fe₃O₄ MNPs could be tailored by adjusting the initial concentration of ammonia water and the molar ratio of Fe²⁺/Fe³⁺ during the preparation process. The H₂O₂-activating ability of Fe₃O₄ MNPs was evaluated by using Rhodamine B (RhB) as a model compound of organic pollutants to be degraded. At pH 5.4 and temperature 40 °C, the sonochemically synthesized Fe₃O₄ MNPs were observed to be able to activate H₂O₂ and remove ca. 90% of RhB (0.02 mmol L^?1) in 60 min with a apparent rate constant of 0.034 min^?1 for the RhB degradation, being 12.6 folds of that (0.0027 min^?1) over the Fe₃O₄ MNPs prepared via a conventional reverse co-precipitation method. The mechanisms of the peroxidase-like catalysis with Fe₃O₄ MNPs were discussed to develop more efficient novel catalysts.