Effect of EtOH/MgCl(2) molar ratios on the catalytic properties of MgCl(2)-SiO(2)/TiCl(4) Ziegler-Natta catalyst for ethylene polymerization

MgCl(2)-SiO(2)/TiCl(4) Ziegler-Natta catalysts for ethylene polymerization were prepared by impregnation of MgCl(2) on SiO(2) in heptane and further treatment with TiCl(4). MgCl(2)·nEtOH adduct solutions were prepared with various EtOH/MgCl(2) molar ratios for preparation of the MgCl(2)-supported and MgCl(2)-SiO(2)-supported catalysts in order to investigate the effect on polymerization performance of both catalyst systems. The catalytic activities for ethylene polymerization decreased markedly with increased molar ratios of EtOH]/MgCl(2)] for the MgCl(2)-supported catalysts, while for the bi-supported catalysts, the activities only decreased slightly. The MgCl(2)-SiO(2)-supported catalyst had relatively constant activity, independent of the EtOH]/MgCl(2)] ratio. The lower EtOH]/MgCl(2)] in MgCl(2)-supported catalyst exhibited better catalytic activity. However, for the MgCl(2)-SiO(2)-supported catalyst, MgCl(2) can agglomerate on the SiO(2) surface at low EtOH]/MgCl(2)] thus not being not suitable for TiCl(4) loading. It was found that the optimized EtOH]/MgCl(2)] value for preparation of bi-supported catalysts having high activity and good spherical morphology with little agglomerated MgCl(2) was 7. Morphological studies indicated that MgCl(2)-SiO(2)-supported catalysts have good morphology with spherical shapes that retain the morphology of SiO(2). The BET measurement revealed that pore size is the key parameter dictating polymerization activity. The TGA profiles of the bi-supported catalyst also confirmed that it was more stable than the mono-supported catalyst, especially in the ethanol removal region.