Thermodynamics of Cr2O3, FeCr2O4, ZnCr2O4, and CoCr2O4

High-temperature heat capacity measurements were obtained for Cr₂O₃, FeCr₂O₄, ZnCr₂O₄, and CoCr₂O₄ using a differential scanning calorimeter. These data were combined with previously available, overlapping heat capacity data at temperatures up to 400 K and fitted to 5-parameter Maier–Kelley C_p(T) equations. Expressions for molar entropy were then derived by suitable integration of the Maier–Kelley equations in combination with recent S^°(298) evaluations. Finally, a database of high-temperature equilibrium measurements on the formation of these oxides was constructed and critically evaluated. Gibbs free energies of Cr₂O₃, FeCr₂O₄, and CoCr₂O₄ were referenced by averaging the most reliable results at reference temperatures of (1100, 1400, and 1373) K, respectively, while Gibbs free energies for ZnCr₂O₄ were referenced to the results of Jacob K.T. Jacob, Thermochim. Acta 15 (1976) 79–87] at T = 1100 K. Thermodynamic extrapolations from the high-temperature reference points to T = 298.15 K by application of the heat capacity correlations gave Δ_fG^°(298) = (?1049.96, ?1339.40, ?1428.35, and ?1326.75) kJ · mol^?1 for Cr₂O₃, FeCr₂O₄, ZnCr₂O₄, and CoCr₂O₄, respectively.