基于MOF (Cu)@biochar气凝胶的制备及其在缓释氮肥上的应用

以羧甲基纤维素(CMC)、明胶和MOF(Cu)@biochar为原料,采用简单有效的冷冻干燥方法制备了(CMC/Gelatin/MOF(Cu)@biochar)杂化气凝胶,并用傅里叶变换红外光谱(FT-IR)、热重分析(TG)、X射线粉末衍射(XRD)、扫描电镜(SEM)和X射线光电子能谱(XPS)技术对其进行了表征;研究了MOF(Cu)@biochar含量、pH和不同的盐水溶液对杂化气凝胶溶胀行为的影响;以该气凝胶负载氯化铵,制备了一种新型缓释肥料(SRF),并研究了含2%(wt)SRF的沙性土壤的保水能力;SRF在土壤中第30天的累积释放率为79.4%;肥料在土壤中释放符合非Fickian扩散和阳离子交换的协同作用机理。     

基于DNA酶催化的卟啉金属化检测锌

利用G-四链体DNA（T30695）催化Zn²⁺插入到中卟啉IX（MPIX）中，引起荧光偏移的特点，建立了检测Zn²⁺的方法。在40μmol/L MPIX、0.6μmol/L Pb²⁺、5μmol/L T30695和1%Triton的最优实验条件下，该方法在Zn²⁺浓度为0.5～5μmol/L范围内呈现良好的线性关系，相关系数R²=0.95，检出限为73.5 nmol/L。离子选择性实验表明该方法对Zn²⁺具有较好的选择性，用于实际样品测定，回收率在94.7%～100.4%之间。     

复合电极La-Ni-B的制备及电催化偏硼酸钠的性能

为进一步提高对偏硼酸钠电催化还原的效率,采用化学镀的方法,以铜片为基体,PdCl2乙醇胶体溶液为活化剂,乙醇为化学镀溶剂,制备了稀土复合电极La-Ni-B.并采用XRD、SEM、EDS方法对催化剂进行表征分析,结果表明稀土合金以纳米颗粒的形式附着在基体表面,所得合金膜是非晶态的.通过循环伏安法研究了复合电极La-Ni-B用于电解偏硼酸钠制备硼氢化钠的可行性.以硼氢化钠实际生产量为指标,探讨了直流、脉冲两种不同供电方式、脉冲电流频率、电解时间对电解行为的影响.结果表明稀土镧对电解偏硼酸钠有催化作用,以20 mL镀液制备的复合电极,在脉冲频率阳极时间T1=1 s,阴极时间T2=1 s时,最佳电解时间为4h.复合电极在重复使用3次的情况下,硼氢化钠产量降低15;,催化剂的重复使用性能良好.     

基于NiCo2O4纳米片电极的非对称混合电容器

The looming global energy crisis and ever-increasing energy demands have catalyzed the development of renewable energy storage systems. In this regard, supercapacitors (SCs) have attracted widespread attention because of their advantageous attributes such as high power density, excellent cycle stability, and environmental friendliness. However, SCs exhibit low energy density and it is important to optimize electrode materials to improve the overall performance of these devices. Among the various electrode materials available, spinel nickel cobaltate (NiCo₂O₄) is particularly interesting because of its excellent theoretical capacitance. Based on the understanding that the performances of the electrode materials strongly depend on their morphologies and structures, in this study, we successfully synthesized NiCo₂O₄ nanosheets on Ni foam via a simple hydrothermal route followed by calcination. The structures and morphologies of the as-synthesized products were characterized by X-ray diffraction, scanning electron microscopy, and Brunauer-Emmett-Teller (BET) surface area analysis, and the results showed that they were uniformly distributed on the Ni foam support. The surface chemical states of the elements in the samples were identified by X-ray photoelectron spectroscopy. The as-synthesized NiCo₂O₄ products were then tested as cathode materials for supercapacitors in a traditional three-electrode system. The electrochemical performances of the NiCo₂O₄ electrode materials were studied and the area capacitance was found to be 1.26 C·cm^-2 at a current density of 1 mA·cm^-2. Furthermore, outstanding cycling stability with 97.6% retention of the initial discharge capacitance after 10000 cycles and excellent rate performance (67.5% capacitance retention with the current density from 1 to 14 mA·cm^-2) were achieved. It was found that the Ni foam supporting the NiCo₂O₄ nanosheets increased the conductivity of the electrode materials. However, it is worth noting that the contribution of nickel foam to the areal capacitance of the electrode materials was almost zero during the charge and discharge processes. To further investigate the practical application of the as-synthesized NiCo₂O₄ nanosheets-based electrode, a device was assembled with the as-prepared samples as the positive electrode and active carbon (AC) as the negative electrode. The assembled supercapacitor showed energy densities of 0.14 and 0.09 Wh·cm^-3 at 1.56 and 4.5 W·cm^-3, respectively. Furthermore, it was able to maintain 95% of its initial specific capacitance after 10000 cycles. The excellent electrochemical performance of the NiCo₂O₄ nanosheets could be ascribed to their unique spatial structure composed of interconnected ultrathin nanosheets, which facilitated electron transportation and ion penetration, suggesting their potential applications as electrode materials for high performance supercapacitors. The present synthetic route can be extended to other ternary transition metal oxides/sulfides for future energy storage devices and systems.     

基于自组装膜的光纤错位型氨气传感器

演示了一种基于单壁碳纳米管（SWCNTs）-聚合物自组装复合膜的光纤错位型氨气传感器。通过层层自组装技术在高Q谐振器上涂覆薄膜，薄膜上存在大量的游离羧基以及较大的比表面积，这提供了光与薄膜之间的强相互作用，以及对氨气的高吸附性和选择性。光谱随氨气浓度影响的有效折射率而变化。在(10～37) ×10?6的低浓度范围内，光谱变化与氨气浓度差之比即灵敏度为13.25 pm/10?6，检测极限为3.77 ×10?6并且具有良好的线性。这项工作研制为低浓度和高选择性氨气传感器提供了一种有效的方法。     

基于气体浓度定量的嗅觉刺激器优化设计

现有的基于磁共振测量的嗅觉刺激器，通过调节嗅剂液体浓度的方法可以实现不同浓度的嗅觉刺激，但随着实验进行，受到嗅剂挥发以及实验环境（温度、湿度、气流量）变化的影响，很难确保输送至鼻腔的嗅剂气体浓度的稳定性，进而影响实验结果的准确性．本研究对本实验室前期开发的嗅觉刺激装置进行改进，实现了气体浓度精确定量．改进后的嗅觉刺激器主要分为三个部分：控制系统、反馈系统和气路系统．控制系统主要实现气路系统的送气控制和嗅剂气体浓度调节；反馈系统则负责对气体浓度进行测量；气路系统则在原有基础上添加活性炭装置，降低无关因素干扰．装置改进之后，不同气路切换时间为75.2 ms，比原装置减少了1 s，有效提高刺激精度．实验结果显示，气体浓度调节前，300 s内乙醇、吡啶、乙酸戊酯嗅剂气体浓度分别下降6.7%、71.4%、79.2%，嗅剂气体浓度短时间内发生较大改变．加入气体浓度调节功能后，当气体浓度下降至目标浓度的90%时，可通过调节气泵电压改变嗅剂气流与空气气流比例，从而调节嗅剂气体浓度至目标值，其中吡啶、乙酸戊酯用时13 s．     

基于电化学发光和阻抗技术研究DNA单碱基错配

单碱基错配的识别和稳定性差异在核酸多态性研究中至关重要。在同一电化学传感器平台上，采用电化学发光（ECL）和电化学阻抗（EIS）2种技术，协同研究DNA链中不同类型和不同位点的单碱基错配识别和稳定性差异。电极表面具有茎环构象的探针DNA与完全互补DNA、不同类型或不同位点单碱基错配DNA杂交前后的ECL和EIS信号强度变化有显著差异。信号强度变化可揭示单碱基错配识别的稳定性。结果表明，DNA链中心位点的C-A单碱基错配稳定性低于链两端的，靠近键合电极表面双链链端的C-A单碱基错配稳定性低于非键合电极表面双链链端的，同一中心位点C-X碱基对的稳定性顺序为C-G?C-T>C-A≥C-C。研究结果可为核酸多态性研究提供参考。     

高居里温度铁电单晶PIN-PT的机电性能

弛豫铁电单晶Pb(In_1/2Nb_1/2)O₃-PbTiO₃(PIN-PT)相较于常用的Pb(Mg_1/3Nb_2/3)O₃-PbTiO₃(PMN-PT)具有更高的居里温度,在高稳定性、高性能的传感器、换能器方面具有应用前景。本工作采用谐振法研究了[001]方向极化的0.66PIN-0.34PT铁电单晶的全矩阵机电性能参数。0.66PIN-0.34PT 单晶的三方-四方相变温度(T_RT)约为160 ℃,居里温度(T_C)约为260 ℃,室温压电系数d₃₃、d₃₁、d₁₅分别为1 340 pC/N、-780 pC/N、321 pC/N,介电常数ε^T₃₃、ε^S₃₃、ε^T₁₁、ε^S₁₁分别为2 700、905、2 210、1 927,机电耦合系数 k₃₃、k₃₁、k₁₅、k_t分别为 87%、58%、38%、61%。其纵向压电常数(d₃₃)和纵向机电耦合系数(k₃₃)小于 PMN-PT 单晶,但是横向压电性能(d₃₁)和剪切压电性能(d₁₅)都略高于PMN-PT单晶。另外,研究了机电耦合性能随温度的变化趋势,发现0.66PIN-0.34PT单晶在150 ℃以下有较好的温度稳定性。