Microwave absorption properties of composite powders with low density

The composites of barium ferrite coated on hollow ceramic microspheres were prepared using sol-gel technique. The crystal structure, morphology and microwave absorption properties of composite powders with different weight ratio of microspheres were studied with XRD, EDS, FESEM and vector network analyzer. The results show that the microwave absorption properties of composite powders are greatly improved. The maximum microwave loss of composite powders reaches 31 dB with an amount of 50 wt.% microspheres, and its density is only about 1.80 g/cm³. The effect of hollow ceramic microspheres on the microwave absorption property is also discussed.     

Lanthanum nitrate decomposition by both temperature programmed heating and citrate gel combustion

Thermal decomposition of lanthanum nitrate to lanthanum oxide was carried out by both temperature programmed heating (TPH) and citrate-gel combustion. The temperature programmed heating was carried out under flow of oxidizing (air), neutral (nitrogen) and reducing (25 vol.% hydrogen+argone mixture) gases, and the processes were controlled by simultaneous thermogravimetry and differential thermal analysis. It was shown that hydrogen atmosphere helps to reduce temperatures of all decomposition steps. The results of TPH were utilized to check the nature of residues in the products of lanthanum nitrate-to-oxide conversion performed via citrate-gel combustion technique.     

Preparation and microwave absorption properties of electroless Co-Ni-P coated strontium ferrite powder

A new type of Co-Ni-P coated strontium ferrite nanocomposite was prepared with electroless plating enhanced by ultrasonic wave at room temperature. The plating process was studied carefully. The morphology, crystal structure and microwave absorption properties of the Co-Ni-P coated powder were studied with field emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), energy dispersive analysis of X-rays (EDX) and vector network analyzer. The results show that the strontium ferrite powder was successfully coated with Co-Ni-P alloy and possesses excellent microwave absorption properties. The maximum microwave loss of the composite powder reaches −44.12 dB. The bandwidth with the loss above −10 dB exceeds 13.8 GHz.     

复合型铁氧体全极化器

应用耦合波理论 ,对有两组NS/N′S′四磁极磁化铁氧体中极化传输进行了分析 .在X、S波段对多种椭圆极化进行了测试 ,还完成了 0°～ 180°范围内多种线极化波测试 .最后对全极化器应用作了简单介绍 .     

纯锆上离子注入钇和镧后的表面分析

用金属蒸汽真空弧源，以40kV加速电压对纯锆样品分别进行了10¹⁶—10¹⁷/cm²的钇、镧离子注入，注入温度约为130℃.然后对注入样品进行表面分析.x射线光电子能谱分析表明，注入的钇以Y₂O₃形式存在，镧以La₂O₃形式存在.俄歇电子能谱表明，纯锆基体表面的氧化膜厚度随着离子注入剂量的增加而增加，当离子注入剂量达到10¹⁷/cm²时，氧化膜的厚度达到了最大值.卢瑟福背散射显示镧层的厚度约为30nm，同时直接观察到当离子注入剂量为(La+Y)10¹⁷/cm²时，纯锆样品表面发生了严重的溅射. 关键词： 纯锆 钇和镧离子共注入 卢瑟福背散射 x射线光电子能谱     

Mössbauer study of nanodimensional nickel ferrite – mechanochemical synthesis and catalytic properties

Iron–nickel spinel oxide NiFe₂O₄ nanoparticles have been prepared by the combination of chemical precipitation and subsequent mechanical milling. For comparison, their analogue obtained by thermal synthesis is also studied. Phase composition and structural properties of iron–nickel oxides are investigated by X-ray diffraction and Mössbauer spectroscopy. Their catalytic behavior in methanol decomposition to CO and methane is tested. An influence of the preparation method on the reduction and catalytic properties of iron–nickel samples is established.     

Effects of pH and citric acid contents on characteristics of ester-derived BaFe12O19 powder

The single domain size of BaFe₁₂O₁₉ powder with crystallite sizes less than 200 nm was produced using a citric acid precursor method. Fe³⁺ and Ba²⁺, in a molar ratio of 12, were chelated by COOH⁻ in an aqueous solution. After ethylene glycol additions, esterification, dehydration, and calcination led to the formation of ester-derived BaFe₁₂O₁₉ powder. High pH and/or high citric acid contents in the starting solution are required to complete chelate metallic ions in the solution and to form pure barium ferrite powder at 1073 K. Pure single magnetic domain BaFe₁₂O₁₉ particles of M(30 kOe)≈54 emu/g, M_r≈28 emu/g, and H_c≈3.7 kOe were produced using [citric acid]/[metallic ions]=1.5 and pH7.     

Effects of microstructure on the temperature dependence of relative initial permeability of NiCuZn ferrites

In the present work, ferrites with compositions of (Ni_0.27Zn_0.64Cu_x)Fe_1.98O₄ (x=0.1, 0.2) were prepared by conventional ceramic methods. The relationship between the microstructure and the temperature dependence of relative initial permeability was investigated. It was found that intergranular pores in the ferrites generate large demagnetizing fields, reducing the temperature dependence of the effective anisotropy field H_eff, and decreasing the temperature dependence of the relative initial permeability accordingly. However, intragranular pores pin the movement of domain walls. Compared with the permeability induced by domain wall motion, the permeability that resulted from the spin rotation is more sensitive to temperature. As a result, the relative initial permeability of ferrites becomes more sensitive to temperature with increasing micropores within grains.     

Synthesis and Structural Characterization of Adduct [La(NO_3)_3·4H_2O]·2(BQEB)

Differentkindsofopenchaincrownethershavebeensynthesizedasthemodelcompoundsofionophoresandtheirinteractionswithsodium,potassiumandrareearthionshavealsobeenstudiedl'z.PanshowedCe(III)yieldedalf1complexwithl,8-bis(8'-quinolyloxy)-3,6-dioxaandtheCe(IIl)ioncoordinatedbothtoetheroxygenandquinolinenitrogenatoms3.TUmInleridentifiedtwolanthanidenitratecomplexeshavingastoichiometryof3:2(3RE:2L)'.InordertostUdythefunctionsofbothquinolineandbenzenering,introducedintothepolyetherchain,a1inearpolyether…