Polymerization behaviors of racemic and chiral amphiphilic monomers in organized bilayer membranes of lamellar liquid crystalline phase

A racemic amphiphilic monomer, n‐dodecyl glyceryl itaconate (DGI), forms bilayer membranes in water in the presence of small amount of ionic cosurfactant and shows iridescent color. A chiral DGI, S‐DGI, also shows an iridescent property, but with a rather red shift in the color, which can be ascribed to the increased packing density of the monomer in the bilayer membranes. Chrial DGI has a more compact packing density than racemic one owing to closer distance between the monomer molecules; the conversion rate, however, is slower than that of racemic one when H₂O₂ is used as an initiator. When the initiator is changed to an amphiphilic one, 4‐(2‐hydroxyethoxy) phenyl‐(2‐hydroxy‐2‐propyl) ketone (Irgacure 2959), the chiral DGI shows even a little faster conversion rate than that of racemic one. The NMR chemical shift results of protons in benzene ring show that the molecules of Irgacure 2959 insert into the bilayer membranes. The molecular weights of the corresponding polymers prove that the initiation by H₂O₂ is restricted compared to that by Irgacure 2959. It is concluded that the decelerated polymerization behavior of chiral DGI initiated by H₂O₂ is a result of limited diffusion of the initiator into the lamellar bilayer structures. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4891–4900, 2007     

Photoinitiated curing of mono‐ and bifunctional epoxides by combination of active chain end and activated monomer cationic polymerization methods

Photoinitiated cationic polymerization of mono‐ and bifunctional epoxy monomers, namely cyclohexeneoxide (CHO), 4‐epoxycyclohexylmethyl‐3′,4′‐epoxycyclohexanecarboxylate (EEC), respectively by using sulphonium salts in the presence of hydroxylbutyl vinyl ether (HBVE) was studied. The real‐time FTIR spectroscopic, gel content determination, and thermal characterization studies revealed that both hydroxyl and vinyl ether functionalities of HBVE take part in the polymerization. During the polymerization, HBVE has the ability to react via both active chain end (ACE) and activated monomer mechanisms through its hydroxyl and vinyl ether functionalities, respectively. Thus, more efficient curing was observed with the addition of HBVE into EEC‐containing formulations. It was also demonstrated that HBVE is effective in facilitating the photoinduced crosslinking of monofunctional epoxy monomer, CHO in the absence of a conventional crosslinker. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4914–4920, 2007     

Radical copolymerization of 2‐trifluoromethylacrylic monomers. II. Kinetics,monomer reactivities,and penultimate effect in their copolymerization with norbornenes and vinyl ethers

Radical copolymerizations of electron‐deficient 2‐trifluoromethylacrylic (TFMA) monomers, such as 2‐trifluoromethylacrylic acid and t‐butyl 2‐trifluoromethylacrylate (TBTFMA), with electron‐rich norbornene derivatives and vinyl ethers with 2,2′‐azobisisobutyronitrile as the initiator were investigated in detail through the analysis of the kinetics in situ with ¹H NMR and through the determination of the monomer reactivity ratios. The norbornene derivatives used in this study included bicyclo[2.2.1]hept‐2‐ene (norbornene) and 5‐(2‐trifluoromethyl‐1,1,1‐trifluoro‐2‐hydroxylpropyl)‐2‐norbornene. The vinyl ether monomers were ethyl vinyl ether, t‐butyl vinyl ether, and 3,4‐dihydro‐2‐H‐pyran. Vinylene carbonate was found to copolymerize with TBTFMA. Although none of the monomers underwent radical homopolymerization under normal conditions, they copolymerized readily, producing a copolymer containing 60–70 mol % TFMA. The copolymerization of the TFMA monomer with norbornenes and vinyl ethers deviated from the terminal model and could be described by the penultimate model. The copolymers of TFMA reported in this article were evaluated as chemical amplification resist polymers for the emerging field of 157‐nm lithography. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1478–1505, 2004     

基于2,5-二(4′-甲酰基苯基)苯乙烯的螺旋链光学活性聚合物的合成与表征

通过2,5-二溴苯乙烯与对甲酰基苯硼酸的Suzuki偶联反应得到2,5-二(4′-甲酰基苯基)苯乙烯.在催化剂量的冰乙酸存在下,与光学纯的(S)-(-)-α-甲基苄胺或(R)-(+)-α-甲基苄胺发生缩和反应,得到了一对手性非外消旋单体,(+)-2,5-二{4-′[(N-(S)-α-甲基苄亚胺基)次甲基]苯基}苯乙烯和(-)-2,5-二{4′-[(N-(R)-α-甲基苄亚胺基)次甲基]苯基}苯乙烯.以偶氮二异丁腈(AIBN)或过氧化苯甲酰(BPO)为引发剂,经自由基溶液聚合得到光学活性聚合物.比旋光度、紫外-可见吸收光谱以及圆二色光谱研究表明,聚合物主链可能形成了某一方向占优的稳定螺旋构象,且该螺旋构象的旋光方向与单体的旋光方向相反.聚合条件对聚合物的光学活性有很大影响,在极性较大的芳香族溶剂和较高温度下得到的聚合物具有和单体相差更大的比旋光度.侧基的手性基团脱除后,聚合物仍具有一定的旋光性,说明聚合过程中形成的螺旋手性具有一定的记忆效应.     

Spherical dye-doped silica particles

Organic dyes such as water soluble porphyrins were incorporated into monodispersed SiO₂ particles using the sol-gel technique (the Stober synthesis) and their monomeric and dimeric properties were investigated by aiming at the microcavity effect. Doping efficiencies of dyes into SiO₂ particles depended on dye's hydrophilic properties. The doping efficiency of a porphyrin, TTMAPP, decreased with increasing the nominal content in the starting solution and the doping content showed the maximum value of 1.6×10^–5 mol/g SiO₂. With increasing the TTMAPP content, spectra of doped particles were changed from dimeric to monomeric nature; the absorption peak due to dimers disappeared and halfwidth of absorption at Soret band decreased. This unusual change was caused by the decrease of particle sizes by dye doping. The TTMAPP-doped sample having monomeric spectrum showed the fluorescence life time of 8.5 nsec and photochemical hole burning at about 5 K.     

Synthesis and application as polymer electrolyte of hyperbranched polyether made by cationic ring‐opening polymerization of 3‐{2‐[2‐(2‐hydroxyethoxy)ethoxy]ethoxymethyl}‐3′‐methyl‐oxetane

A novel cyclic ether monomer 3‐{2‐[2‐(2‐hydroxyethoxy)ethoxy]ethoxy‐methyl}‐3′‐methyloxetane (HEMO) was prepared from the reaction of 3‐hydroxymethyl‐3′‐methyloxetane tosylate with triethylene glycol. The corresponding hyperbranched polyether (PHEMO) was synthesized using BF₃·Et₂O as initiator through cationic ring‐opening polymerization. The evidence from ¹H and ¹³C NMR analyses revealed that the hyperbranched structure is constructed by the competition between two chain propagation mechanisms, i.e. active chain end and activated monomer mechanism. The terminal structure of PHEMO with a cyclic fragment was definitely detected by MALDI‐TOF measurement. A DSC test implied that the resulting polyether has excellent segment motion performance potentially beneficial for the ion transport of polymer electrolytes. Moreover, a TGA assay showed that this hyperbranched polymer possesses high thermostability as compared to its liquid counterpart. The ion conductivity was measured to reach 5.6 × 10^?5 S/cm at room temperature and 6.3 × 10^?4 S/cm at 80 °C after doped with LiTFSI at a ratio of Li:O = 0.05, presenting the promise to meet the practical requirement of lithium ion batteries for polymer electrolytes. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3650–3665, 2006     

Synthesis and polymerization of a new nitrogen‐containing bis‐ortho‐diynylarene monomer

This study focuses on the preparation, characterization, and optical properties of new bis(3,4‐diphenylethynylphenyl)phenylamine. This is the first nitrogen‐containing bis‐ortho‐diynylarene (BODA) monomer having a nitrogen atom as the spacer group. BODA monomers are usually prepared from common bisphenols, thereby providing great synthetic versatility and the opportunity to develop a wide array of novel polyarylene thermosets by varying the aromatic spacer group. The new bis(3,4‐bisphenylethynylphenyl)phenylamine was synthesized in five steps. This compound emits an intense blue color (λ = 438 nm) upon irradiation by UV light and may be suitable for use as an emitting layer in electroluminescent devices. Bis‐(3,4‐bisphenylethynylphenyl)phenylamine and its polymer have photoluminescence quantum yields 34 and 38%, respectively, and long excited‐state lifetimes of 3.2 and 3.6 ns, respectively. The structure of the monomer and its polymer were characterized using spectroscopic techniques including Ultraviolet–visible Spectrophotometer, Photoluminescence Spectrophotometer, Fourier Transform infrared spectroscopy, and Gel Permeation Chromatography. The polymerizations were studied by Differential Scanning Calorimeter. The amount of weight loss and the thermostability of the nitrogen‐containing polymer were determined from thermogravimetric analysis. The electrical conductivity of neat HCl‐doped BODA‐derived polymer film was measured according to the standard four‐point probe technique. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6988–6996, 2006     

Radiation induced synthesis and swelling characterization of thermo-responsive N-isopropylacrylamide-co-ionic hydrogels

Two-component thermo-responsive hydrogels poly(N-isopropylacrylamide)-co-vinylbenzyltrimethylammonium chloride (NIPA-co-VBT) and poly(N-isopropylacrylamide)-co-p-sodium styrene sulphonate (NIPA-co-SSS) were prepared by using high energy gamma radiation. The gels were characterized by Fourier transformed infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and sol-gel analysis. The presence of ionic monomers in NIPA leads to lower gel content. Introduction of ionic components in the matrix enhanced swelling extent but caused slower volume transition. The swelling studies in alcohol indicated that swelling extent was function of polarity of the swelling medium and all gels followed the order water > methanol > ethanol > iso-propanol. In mixed co-solvents (water-alcohol), they exhibit complex reentrant behavior. The co-polymer gels containing VBT swelled faster and to higher extent than those containing SSS. The dynamic swelling studies indicated that diffusion of water in PNIPA gel shifts from Fickian for PNIPA to anomalous for NIPA-co-ionic gels also the mean swelling time (MST) decreases for gels containing ionic monomers.