籽晶{100}面形状对高温高压合成金刚石大单晶的影响

选用不同形状的{100}金刚石籽晶面,以NiMnCo合金为触媒,利用温度梯度法在压力为5.5 GPa、温度为1260～1300℃的条件下,合成Ib型金刚石大单晶。通过光学显微镜和电子显微镜对晶体的形貌进行表征。研究发现,将合成籽晶的{100}晶面切割成不同形状,只会令晶体的长宽比发生改变,晶体并不会因籽晶形状的改变而偏离{100}晶体的正常形貌。晶体的合成质量受到籽晶长宽比的影响:在籽晶长宽比较小的情况下,晶体的合成质量能够得到保证;但当籽晶长宽比过大时,合成晶体的下表面出现较多缺陷。关于籽晶形状对晶体生长情况影响的研究,揭示了籽晶形状与合成晶体形貌之间的关系,有利于更深入理解晶体的生长过程和外延生长机理,对于今后合成不同形貌的金刚石具有借鉴意义。同时此项研究有助于扩大籽晶的选取范围,降低籽晶的选择难度,提升工业级金刚石的利用率,为合成金刚石大单晶的籽晶选取提供了技术支持。     

Growth of gem-grade nitrogen-doped diamond crystals heavily doped with the addition of Ba（N3）2

Additive Ba(N 3) 2 as a source of nitrogen is heavily doped into the graphite-Fe-based alloy system to grow nitrogendoped diamond crystals under a relatively high pressure (about 6.0 GPa) by employing the temperature gradient method.Gem-grade diamond crystal with a size of around 5 mm and a nitrogen concentration of about 1173 ppm is successfully synthesised for the first time under high pressure and high temperature in a China-type cubic anvil highpressure apparatus.The growth habit of diamond crystal under the environment with high degree of nitrogen doping is investigated.It is found that the morphologies of heavily nitrogen-doped diamond crystals are all of octahedral shape dominated by {111} facets.The effects of temperature and duration on nitrogen concentration and form are explored by infrared absorption spectra.The results indicate that nitrogen impurity is present in diamond predominantly in the dispersed form accompanied by aggregated form,and the aggregated nitrogen concentration in diamond increases with temperature and duration.In addition,it is indicated that nitrogen donors are more easily incorporated into growing crystals at higher temperature.Strains in nitrogen-doped diamond crystal are characterized by micro-Raman spectroscopy.Measurement results demonstrate that the undoped diamond crystals exhibit the compressive stress,whereas diamond crystals heavily doped with the addition of Ba(N 3) 2 display the tensile stress.     

Synthesis and characterization of p-type boron-doped IIb diamond large single crystals

High-quality p-type boron-doped IIb diamond large single crystals are successfully synthesized by the temperature gradient method in a china-type cubic anvil high-pressure apparatus at about 5.5 GPa and 1600 K.The morphologies and surface textures of the synthetic diamond crystals with different boron additive quantities are characterized by using an optical microscope and a scanning electron microscope respectively.The impurities of nitrogen and boron in diamonds are detected by micro Fourier transform infrared technique.The electrical properties including resistivities,Hall coefficients,Hall mobilities and carrier densities of the synthesized samples are measured by a four-point probe and the Hall effect method.The results show that large p-type boron-doped diamond single crystals with few nitrogen impurities have been synthesized.With the increase of quantity of additive boron,some high-index crystal faces such as {113} gradually disappear,and some stripes and triangle pits occur on the crystal surface.This work is helpful for the further research and application of boron-doped semiconductor diamond.     

Synthesis of N-type semiconductor diamonds with sulfur,boron co-doping in FeNiMnCo-C system at high pressure and high temperature

A series of diamonds with boron and sulfur co-doping were synthesized in the Fe Ni Mn Co-C system by temperature gradient growth(TGG) under high pressure and high temperature(HPHT). Because of differences in additives, the resulting diamond crystals were colorless, blue-black, or yellow. Their morphologies were slab, tower, or minaret-like. Analysis of the x-ray photoelectron spectra(XPS) of these diamonds shows the presence of B, S, and N in samples from which N was not eliminated. But only the B dopant was assuredly incorporated in the samples from which N was eliminated. Resistivity and Hall mobility were 8.510 ?·cm and 760.870 cm~2/V·s, respectively, for a P-type diamond sample from which nitrogen was eliminated. Correspondingly, resistivity and Hall mobility were 4.211×10~5 ?·cm and 76.300 cm~2/V·s for an N-type diamond sample from which nitrogen was not eliminated. Large N-type diamonds of type Ib with B–S doping were acquired.     

Large single crystal diamond grown in FeNiMnCo-S-C system under high pressure and high temperature conditions

Large diamonds have successfully been synthesized from FeNiMnCo-S-C system at temperatures of 1255-1393 ℃and pressures of 5.3-5.5 GPa.Because of the presence of sulfur additive,the morphology and color of the large diamond crystals change obviously.The content and shape of inclusions change with increasing sulfur additive.It is found that the pressure and temperature conditions required for the synthesis decrease to some extent with the increase of S additive,which results in left down of the V-shape region.The Raman spectra show that the introduction of additive sulfur reduces the quality of the large diamond crystals.The x-ray photoelectron spectroscopy(XPS) spectra show the presence of S in the diamonds.Furthermore,the electrical properties of the large diamond crystals are tested by a four-point probe and the Hall effect method.When sulfur in the cell of diamond is up to 4.0 wt.%,the resistance of the diamond is 9.628×10~5 Ω·cm.It is shown that the large single crystal samples are n type semiconductors.This work is helpful for the further research and application of sulfur-doped semiconductor large diamond.     

Dependence of Crystal Quality and β Value on Synthesis Temperature in Growing Gem Diamond Crystals

High quality Ib gem diamond single crystals were synthesized in cubic anvil high-pressure apparatus （SPD- 6 × 1200） under 5.4GPa and 1230℃-1280℃. The （100） face of seed crystal was used as growth face, and Ni70Mn25Co5 alloy was used as solvent/catalyst. The dependence of crystal quality andβ value （the ratio of height to diameter of diamond crystal） on synthesis temperature was studied. When the synthesis temperature is between 1230℃ and 1280℃, theβ value of the synthetic high-quality gem diamond crystals is between 0.4 and 0.6. The results show that when theβ value is between 0.4 and O. 45, the synthetic diamonds are sheet-shape crystals; however, when theβ value is between 0.45 and 0.6, the synthetic diamonds are tower-shape crystals. In addition, when theβ value is less than 0.4, skeleton crystals will appear. When theβ value is more than 0.6, most of the synthetic diamond crystals are inferior crystals.     

含氢添加剂对合成cBN的影响及腔体温度分布

 通过对Li基触媒下立方氮化硼的高温高压合成实验结果的分析,研究了在Li基触媒作为主要触媒及氢化物作为添加剂的环境下,立方氮化硼的生长情况。同时由合成后样品中立方氮化硼的生成区域对V型生长区温度梯度分布进行了分析讨论。     

Effect of FeS doping on large diamond synthesis in FeNi-C system

The large single-crystal diamond with FeS doping along the(111) face is synthesized from the FeNi–C system by the temperature gradient method(TGM) under high-pressure and high-temperature(HPHT). The effects of different FeS additive content on the shape, color, and quality of diamond are investigated. It is found that the(111) face of diamond is dominated and the(100) face of diamond disappears gradually with the increase of the FeS content. At the same time, the color of the diamond crystal changes from light yellow to gray-green and even gray-yellow. The stripes and pits corrosion on the diamond surface are observed to turn worse. The effects of FeS doping on the shape and surface morphology of diamond crystal are explained by the number of hang bonds in different surfaces of diamond. It can be shown from the test results of the Fourier transform infrared(FTIR) spectrum that there exists an S element in the obtained diamond. The N element content values in different additive amounts of diamond are calculated. The XPS spectrum results demonstrate that our obtained diamond contains S elements that exist in S–C and S–C–O forms in a diamond lattice. This work contributes to the further understanding and research of FeS-doped large single-crystal diamond characterization.     

Influence of annealing treatment on as-grown Ib-type diamond crystal at a high temperature and high pressure

In this paper,we report on the influence of annealing treatment on as-grown Ib-type diamond crystal under high pressure and high temperature in a china-type cubic anvil high-pressure apparatus.Experiments are carried out at a pressure of 7.0 GPa and temperatures ranging from 1700 C to 1900 C for 1 h.Annealing treatment of the diamond crystal shows that the aggregation rate constant of nitrogen atoms in the as-grown Ib-type diamond crystal strongly depends on diamond morphology and annealing temperature.The aggregation rate constant of nitrogen remarkably increases with the increase of annealing temperature and its value in octahedral diamond is much higher than that in cubic diamond annealed at the same temperature.The colour of octahedral diamond crystal is obviously reduced from yellow to nearly colorless after annealing treatment for 1 h at 1900 C,which is induced by nitrogen aggregation in a diamond lattice.The extent of nitrogen aggregation in an annealed diamond could approach approximately 98% indicated from the infrared absorption spectra.The micro-Raman spectrum reveals that the annealing treatment can improve the crystalline quality of Ib-type diamond characterized by a half width at full maximum at first order Raman peak,and therefore the annealed diamond crystals exhibit nearly the same properties as the natural IaA-type diamond stones of high quality in the Raman measurements.     

Effects of carbon convection field on large diamond growth under high-pressure high-temperature conditions

Large diamond crystals were successfully synthesized by FeNi-C system using temperature gradient method under high-pressure high-temperature conditions. The assembly of the growth cell was improved and the growth process of diamond was investigated. Effects of the symmetry of carbon convection field around the growing diamond crystal were investigated systematically by adjusting the position of seed crystal in the melted catalyst/solvent. The results indicate that morphologies and metal inclusion distributions of the synthetic diamond crystals vary obviously in both symmetric and non-symmetric carbon convection fields with temperature. Moreover, finite element method was applied to analyze carbon convection mode of the melted catalyst/solvent around the diamond crystal. This work is helpful for understanding the growth mechanism of diamond.