The properties of GaMnN lms grown by metalorganic chemical vapour deposition using Raman spectroscopy

An investigation of room-temperature Raman scattering is carried out on ferromagnetic semiconductor GaMnN films grown by metalorganic chemical vapour deposition with different Mn content values. New bands around 300 and 669 cm^-1, that are not observed in undoped GaN, are found. They are assigned to disorder-activated mode and local vibration mode (LVM), respectively. After annealing, the intensity ratio between the LVM and E₂(high) mode, i.e., I_LVM=I_E2(high), increases. The LO phonon-plasmon coupled (LOPC) mode is found in GaMnN, and the frequency of the LOPC mode of GaMnN shifting toward higher side is observed with the increase in the Mn doping in GaN. The ferromagnetic character and the carrier density of our GaMnN sample are discussed.     

Mid-gap photoluminescence and magnetic properties of GaMnN films grown by metal–organic chemical vapor deposition

Metal-organic chemical vapor deposition （MOCVD） grown ferromagnetic GaMnN films are investigated by photo- luminescence （PL） measurement with a mid-gap excitation wavelength of 405 nm. A sharp PL peak at 1.8 eV is found and the PL intensity successively decreases with the addition of Mn, in which the Mn concentration of sample A is below 1% （[Mn]A =0.75%） but its PL intensity is stronger than other samples＇. The 1.8-eV PL peak is attributed to the recombination of electrons in the t2 state of the neutral Mn3＋ acceptor with holes in the valence band. With Mn concentration increasing, the intensity of the PL peak decreases and the magnetic increment reduces in our samples. The correlation between the PL peak intensity and ferromagnetism of the samples is discussed in combination with the experimental results.     

The properties of GaMnN films grown by metalorganic chemical vapour deposition using Raman spectroscopy

An investigation of room-temperature Raman scattering is carried out on ferromagnetic semiconductor GaMnN films grown by metalorganic chemical vapour deposition with different Mn content values. New bands around 300 and 669 cm-1, that are not observed in undoped GaN, are found. They are assigned to disorder-activated mode and local vibration mode (LVM), respectively. After annealing, the intensity ratio between the LVM and E2 (high) mode, i.e., ILVM /IE2 (high) , increases. The LO phonon-plasmon coupled (LOPC) mode is found in GaMnN, and the frequency of the LOPC mode of GaMnN shifting toward higher side is observed with the increase in the Mn doping in GaN. The ferromagnetic character and the carrier density of our GaMnN sample are discussed.