光谱型椭偏仪精确表征非晶吸收薄膜的光学常数

采用光谱型椭偏仪(SE)和分光光度计分别测量了超薄类金刚石(DLC)薄膜和非晶硅(a-Si)薄膜的椭偏参数(y和D)和透射率T。由于薄膜的厚度与折射率、消光系数之间存在强烈的相关性,仅采用椭偏参数拟合,难以准确得到薄膜的光学常数。如果加入透射率同时进行拟合(以下简称SE+T法),可简单、快速得到薄膜的厚度和光学常数。但随机噪声、样品表面的轻微污染或衬底上任何小的吸收都可能影响SE+T法拟合的光学常数的准确性。因此将SE+T法和光学常数参数化法联用,实现DLC、a-Si薄膜光学常数的参数化,以消除测量数据中的噪声对光学常数的影响。结果显示,联用时的拟合结果具有更好的唯一性,而且拟合得到的光学常数变得平滑、连续且符合Kramers-Kronig(K-K)关系。这种方法特别适合于精确表征厚度仅为几十纳米的非晶吸收薄膜的光学常数。     

兰州重离子加速器冷却储存环中电子冷却性能

为了在兰州重离子加速器冷却储存环(HIRFL-CSR)上开展一维离子束序化的研究,在CSR主环上,对6.39 MeV/u的58Ni19+离子束进行了冷却累积实验。测量了离子束与电子束之间不同的水平、垂直夹角以及不同电子束剖面的情况下,束流累积及束流寿命变化情况;重点研究了离子束衰减过程中动量分散随离子数的变化规律,拟合计算得到了动量分散随离子数按照幂函数衰减的指数;在给定离子数的情况下,动量分散随夹角、电子束剖面的依赖关系,为下一步在CSR上获得纵向一维有序化离子束的研究做准备。在实验中观测到在较大的夹角情况下,离子束出现纵向振荡和中心频率移动。     

Charge stripping accumulation of light heavy ions in HIRFL-CSR main ring

The charge stripping injection method has been adopted for the accumulation of light heavy ions in HIRFL-CSR. This method has some special requirements for the accelerating particles, and at the same time the structure of the injection orbit has to be changed. In this paper, the design of the orbit has been presented, as well as the calculation of the beam line matching. According to the result of commissioning, stripping injection can accumulate the beam to a higher current.     

CuHg_2Ti型Ti_2Cr基合金的电子结构、能隙起源和磁性研究

利用第一性原理计算方法,研究了CuHg2Ti结构下Ti2CrK(K=Sb,Ge,Sn,Sb,Bi)系列合金的电子结构、能隙起源和磁性.研究发现:Ti2CrK(K=Si,Ge)合金是普通半导体材料;Ti2CrK(K=Si,Bi)合金是亚铁磁性半金属材料,其半金属性能隙受到Sb和Bi原子s态的直接影响;Ti2CrSn合金是完全补偿的亚铁磁性半导体.基于Ti2CrSn合金两个自旋方向上的能隙起源不同,通过Si和Ge替换掺杂同族Sn元素调制能隙的宽度,获得了完全补偿亚铁磁性自旋无能隙材料;通过Fe和Mn替换掺杂过渡族Cr元素获得了一系列半金属材料.Ti2Cr1-xFexSn和Ti2Cr1-xMnxSn合金都具有亚铁磁性.所研究的这些半金属性合金的分子磁矩Mtotal与总的价电子数Zt服从Mtotal=Zt-18规则.     

基于量子阱结构的混合型白光有机发光器件

以荧光材料BePP2结合量子阱作为蓝光发射层,磷光材料GIrl和R-4B掺入到混合双极性主体材料CBP∶Bphen中分别作为绿、红发光层并且在红绿发光层中引入间隔层TPBI,组合得到发白光的混合型有机发光器件。其中量子阱是以BePP2作为势阱、TCTA为势垒。结果表明:当势垒层数为2时,器件的最大发光亮度和电流效率分别为21 682.5 cd/m2和23.73 cd/A;当电压从7 V增加到14 V时,色坐标从(0.345,0.350)变化到(0.340,0.342)。与无量子阱结构的参考器件相比,势垒层数为2的器件的最大功率效率为8.07 lm/W,色坐标变化相对最小为±(0.005,0.008),还有一个高的显色指数83。     

BRing中电荷交换引起的束流损失分布模拟计算

在强流重离子加速器运行中，带电粒子与真空管道中的残余气体分子相互作用发生的电荷交换反应是影响重离子束流寿命的关键因素。这种电荷交换过程导致的束流损失将解吸出真空管壁上吸附的气体分子，进而引起真空压力的动态变化，将严重影响加速器的稳定运行和最终束流引出流强。中国科学院近代物理研究所将在广东省惠州市建造的强流重离子加速器装置（High Intensity heavy-ion AcceleratorFacility，简称HIAF）利用增强器（Booster Ring，简称BRing）提供束流流强高达2×1011 ppp的238U35+用于核物理及原子物理等实验研究。对强流重离子加速器BRing中238U35+束流发生电荷交换反应，损失一个电子成为238U36+的过程进行了追踪模拟，计算得到了U36+损失前的运动径迹和全环粒子损失位置分布，模拟结果显示U36+受到色散元件的影响，将集中损失在位于二极磁铁后的漂移节区域中。基于模拟结果，在束流损失位置处设计安装由低解吸率材料制作的准直器，优化设计后的准直效率高达95%以上；并模拟计算了有无准直器时真空压力和束流流强的变化，安装准直器后BRing的平均真空度变化小于10%，将确保BRing加速器的稳定运行。During heavy ion accelerator operation, the charge exchange effect between ions and residual gas molecules is the key factor to influence beam lifetime. The charge exchange process has ions lost on the wall and leads to a dynamical vacuum change, which will seriously affect the accelerator operation and reduce the extraction beam intensity. The Institute of Modern Physics' future project, called High Intensity heavy ion Accelerator Facility (HIAF), will be built in Huizhou city, Guangdong Province, China. The Booster Ring (BRing) will provide 2×11 ppp 238U35+ for nuclear physics experiments. This article studies the track of particle U36+ before impacting on the wall, which is the reference particle U35+ losing one electron, and gets the U36+ loss distribution along the BRing. The simulation result shows that U36+ will be influenced seriously by dispersion elements, and will be lost in the drift sections after the dipoles. Collimators made out of materials with low desorption will be installed in the particles lost positions. The collimator efficiency after optimization can be larger than 95%. It also shows BRing average pressure change and beam intensity change between collimators on and off. The result points out that the BRing average pressure change will be less than 10% with collimators on, which makes BRing operate stably.     

水工结构高强钢筋混凝土梁受剪性能试验研究

通过对12根配置高强箍筋的混凝土梁在集中荷载作用下的受剪试验,研究梁的挠度、箍筋应变、斜裂缝扩展规律及破坏形态。依据现行《水工混凝土结构设计规范》,对比分析试验梁斜截面承载力及考虑荷载长期作用的正常使用阶段斜裂缝宽度。研究结果表明,配置高强箍筋的混凝土梁斜向开裂规律和受力特征与普通钢筋混凝土梁基本相同,受剪承载力可按现行《水工混凝土结构设计规范》公式计算,且有较高安全储备。当考虑荷载长期作用,HRBF500钢筋在水工结构中抗拉强度设计值取360MPa时,斜裂缝宽度满足正常使用极限状态要求。     

HIRFL-CSR commissioning in 2006 and 2007

HIRFL-CSR, a new heavy ion cooler-storage-ring system at IMP, had been in commissioning since the beginning of 2006. In the two years of 2006 and 2007 the CSR commissioning was finished, including the stripping injection (STI), electron-cooling with hollow electron beam, C-beam stacking with the combination of STI and e-cooling, the wide energy-range synchrotron ramping from 7 MeV/u to 1000 MeV/u by changing the RF harmonic-number at mid-energy, the multiple multi-turn injection (MMI), the beam accumulation with MMI and e-cooling for heavy-ion beams of Ar, Kr and Xe, the fast extraction from CSRm and single-turn injection to CSRe, beam stacking in CSRe and the RIBs mass-spectrometer test with the isochronous mode in CSRe by using the time-of-flight method.     

基于β-环糊精单分散银纳米粒子的绿色合成

以硝酸银为原料,β-环糊精为还原剂和保护剂,一步法合成了粒径为10~30 nm的单分散银纳米粒子,其结构经UV-Vis,FT-IR,XRD和TEM表征。研究了pH、反应温度和γ[n(1)∶n(AgNO_3)]对反应的影响,并提出了银纳米粒子的形成机制。     

水热法硼磷改性多孔炭及其电化学性能研究

采用水热法硼磷改性椰壳多孔炭,并对其电化学性能进行研究。通过X射线衍射、红外光谱以及氮气吸脱附表征改性前后多孔炭的结构和性能;将多孔炭制作电化学电容器负极,通过恒流充放电、循环伏安以及交流阻抗测试分析其电化学性能。结果表明,水热法硼磷改性使多孔炭的微观结构及组成发生了一定变化,比电容等电化学性能有明显的提高。渗硼剂为氧化硼,渗硼量为15(wt)%时,比电容达108 F/g,比原始样增长了92%;渗硼剂为硼酸,渗硼量为25(wt)%时,比电容达到98 F/g,比原始样增长了83%。