[ZnO(0.5 nm)/Co(0.6 nm)]60 multilayers were fabricated by magnetron sputtering. The magnetic, transport and optical properties were studied. The ferromagnetic state at low temperature was demonstrated. Most of the grains in the samples will be unblocked when temperature is below 50K. The measured magneto-resistance at 4.8K is higher than 30%. This value is larger than any other reported data. The transport mechanism may come down to a combination of tunnelling conduction with the second-order hopping. Some small peaks on transmittance curves were found, the matter is still open. 相似文献
2.
3.
La0.5-xNdxBa0.5CoO3化合物的磁性和输运特性 总被引:8,自引:4,他引:4
在La0.5-xNdxBa0.5CoO3化合物中用Nd对La进行了替代研究,结果表明,Nd的掺入未改变Co3d电子的巡游性。随Nd含量增大,材料的分子磁矩单调下降,当Nd含量大于或等于0.45时,材料中出现了磁性相分离,当x≤0.45时,随Nd含量增加,材料的居里温度单调下降,这是由于稀土离子的尺寸效应。电阻测量表明,在所研究的温度范围内,在居里点以下,材料属热扩散导电,在居里点以上属极化子的变程跳跃导电。 相似文献
4.
5.
6.
La0.5Ba0.5CoO3中Y的替代效应 总被引:5,自引:3,他引:2
用固相反应法制备了La0.5Ba0.5CoO3多晶材料,系统研究了Y的替代对材料磁性和输运特性的影响,结果发现,Y的掺入主要产生了两种效应,一是Y向Co的3d轨道产生了电荷转移,使分子磁矩下降,二是出现了Co离子的反铁磁交换作用,当Y含量少于或等于0.3时,材料中出现了自旋的非共线结构。当Y含量大于0.3时,材料从铁磁态为主转变为反铁磁态为主,对不同Y含量的材料,其导电机制都属于极化子的变程跳跃导电,随Y含量增加,材料电经迅速增大。 相似文献
7.
La0.7Ca0.3MnO3中的双交换作用与小极化子效应 总被引:1,自引:0,他引:1
本文研究了La0.7Ca0.3MnO3多晶样品的输运性质、电子顺磁共振(EPR)谱随温度的变化规律.实验发现,材料电阻率、热电势在居里温度附近各形成一个尖锐的峰,而在居里温度上、下有着完全不同的变化规律,EPR谱结果也与之完全吻合.可以认为在居里温度以下双交换作用使eg电子退局域而减小电阻率;而在居里温度以上由Jahn-Teller晶格畸变形成的小极化子使eg电子局域化而增大电阻率.进而证实是双交换作用和小极化子效应共同导致了CMR效应的出现. 相似文献
8.
研究了Nd1-xBaxMnO3和La0.67Mg0.33Mn0.85M0.15O3(M=Mn,Ga,Fe)的导电性,发现Mn位的自旋磁矩排列状态和大小对体系的导电性有强烈的影响.在Nd1-xBaxMnO3中,当Mn3+/Mn4+的浓度比值为2∶1,1∶1,1∶2时,电阻率出现半导体-金属转变.推论该类体系的导电性首先由体系中Mn3+和Mn4+自旋磁矩形成的磁结构状态决定,然后才取决于由Ba掺杂浓度所决定的载流子浓度.在La0.67Mg0.33Mn0.85M0.15O3(M=Mn,Ga,Fe)中,Mn位自旋磁矩大小的改变对导电性有强烈的影响,另外发现该类体系均以变程跳跃模式进行导电. 相似文献
9.
本文详细研究了La0.67Sr0.33Mn0.90Fe0.10O3多晶样品的磁电阻和电子自旋共振谱的特性,发现由于Fe离子的掺入,体系的转变温度明显降低,而且磁电阻的峰位偏离了电阻的峰位,另外在高温处磁电阻又出现了另一峰,这些都是由于铁离子改变屯体系的磁性相互作用以及电子可以在Fe离子eg↑态和Mn离子eg↑态之间跃迁而导致的结果,电子自旋共振实验进一步证实了铁离子的在体系中的作用。 相似文献