IntroductionRecently ,wehavereportedthecoordinationchem istryof 1,2 naphthoquinone mono oxime (nqoH)towardsplatinumgroupmetalsincludingrutheniumandrhodi um .1 8ThereactionsofnqoHwithrutheniumcarbonyl[Ru3(CO) 12 ]leadtofiveisomersofmononuclearrutheni umcarbonylcomplexesof 1,2 naphthoquinone mono oxime .1 3Thepresenceoftheliablecarbonylligandsofferstheopportunitytointroduceavarietyofligandswithspe cificfunctionalgroupsintothemolecule .3Bythisstrategy ,metal containingpolymers ,supramolecular…     

水雾化制备Fe74Al4Sn2P10C2B4Si4非晶合金粉末及其磁粉芯性能研究

采用水雾化方法制备Fe7Al4Sn2P10C2B4Si4合金粉末,研究发现该合金具有强的非晶形成能力和高热稳定性,在粉末粒度小于400目时可以形成非晶态合金.采用该非晶粉末制备的磁粉芯在高频下品质因数显著高于MPP粉芯,说明该磁粉芯高频损耗较低.分析表明,非晶合金磁粉芯高频下损耗低的主要原因是电阻率较高.     

表面效应对γ-Fe2O3微粉饱和磁化强度的影响

我们制备了直径为80—700A的γ-Fe₂O₃微粉,测量了它的比饱和磁化强度σ_s和比表面积S_a,得出经验公式:σ_s(s=σ_s(∞)(1—aS_a)。假定微粉由两部分组成:第一部分是表面层,在磁场的作用下,它的磁矩只能转到与磁场成某个角度;第二部分是内部,它的磁矩可以转到磁场的方向。从这个简单的模型出发,上述的经验公式可以得到较好的解释。 关键词：     

超细颗粒γ-Fe_2O_3微粉包钴前后的各向异性

本工作利用穆斯堡尔谱并配合其它研究手段,测量了超细γ-Fe_2O_3微粉在包钴和不包钴两种情况下的各向异性常数K;观察到前者比后者的各向异性常数K增加30％左右。对普通针状包钴型γ-Fe_2O_3磁粉矫顽力增大的原因提供了进一步的说明。     

包钴铁氧体型γ-Fe_2O_3磁粉穆斯堡尔效应的研究

包钴铁氧体型,γ-Fe_2O_3磁粉(简记为CoFe-γ-Fe_2O_3)是针状γ-Fe_2O_3磁粉与Co~( )和Fe~( )溶液起反应,在每个针状颗粒上包覆了一层钴铁氧体固溶体。经此种方法处理后的γ-Fe_2O_3磁粉的矫顽力及其它磁特性有较大的提高。如矫顽力由原来415Oe增加到715Oe;剩磁和矫顽力随时间及温度变化小等。我们利用穆斯堡尔效应并配合其它研究手段进行了研究,认为:CoFe-γ-Fe_2O_3磁粉矫顽力的提高,主要是由于γ-Fe_2O_3磁粉表面包覆了一层钴铁氧体固溶体,γ-Fe_2O_3与钴铁氧体固溶体之间发生磁耦合作用之故。     

包钴型γ-Fe2O3磁粉矫顽力的研究

包钴型γ-Fe₂O₃磁粉分为包钴γ-Fe₂O₃(简记为Co-γ-Fe₂O₃)和包钴包亚铁γ-Fe₂O₃(简记为CoFe-γ-Fe₂O₃)两种,它们的矫顽力可比γ-Fe₂O₃磁粉的提高100至400Oe左右,本工作对这两种磁粉矫顽力增大的原因作了探讨,认为它们矫顽力增大的机制不同:CO-γ-Fe₂O₃矫顽力增大是由于表面包覆一层Co(OH)₂使表面各向异性增大,而CoFe-γ-Fe₂O₃则是由于表面包覆的是钴铁氧体,γ-Fe₂O₃与钴铁氧体之间发生耦合作用,使矫顽力增大。     

超细颗粒γ-Fe2O3微粉包钴前后的各向异性

本工作利用穆斯堡尔谱并配合其它研究手段,测量了超细γ-Fe₂O₃微粉在包钴和不包钴两种情况下的各向异性常数K;观察到前者比后者的各向异性常数K增加30％左右。对普通针状包钴型γ-Fe₂O₃磁粉矫顽力增大的原因提供了进一步的说明。 关键词：     

Development and Evaluation of Gold 3D Cylindrical Nanoelectrode Ensembles

Gold 3D cylindrical nanoelectrode ensembles （NEEs）, 100 nm in diameter and 500 nm in length were prepared by electroless template synthesis in polycarbonate filter membranes, followed by selective controlled chemical etching. The morphology of the nanowires and cylindrical NEEs was imaged by scanning electron microscopy. The protruding nanoelectrodes were in good parallel order. EDX study showed that the nanoelectrode elements consisted of pure gold. The electrochemical evaluation of the 3D electrodes was conducted using the well known [Fe（CN）6]^3-/[Fe（CN）6]^4- couple. Cyclic voltammgrams （CV） show a very low double layer charging current and a higher ratio of signal to background current than 2D disc NEEs. Electrochemical impedance spectroscopy （EIS） indicates that the 3D cylindrical NEEs effectively accelerate the charge transfer process, which is in consistent with the results of CV. The linear relationship with a slope of 0.5 between lg Ipc and lg v shows that linear diffusion is dominant on the 3D cylindrical NEEs at conventional scan rates.     

连续热压

加压烧结是一种新工艺.目前,工业和实验室采用的压力因受模具抗张强度的限制,大约是200公斤/厘米2左右.进一步提高压力有助于降低烧结温度,缩短烧结时间,获得接近理论密度的烧结体.菲利浦公司建立过一种连续热压装置,压力可达1000公斤/厘米2,它是靠六个油缸支持一个六棱柱形的氧化铝模筒承受高医,虽然设备比较复杂,但由于具有压力高及连续烧结的特点,受到了高压研究工作者的重视. 我们采用叶腊石受热膨胀产生的支撑力,使高温氧化铝陶瓷模筒可在1200℃承受2000公斤/厘米2的压力,并以可移动的上、下压杆实现连续加压烧结. 模具结构如图1所示.…     

Fe4N合金的各向异性超精细相互作用

用相干式自旋回波方法观察到Fe₄N合金中的⁵⁷Fe核磁共振谱.各向异性超精细相互作用及畴壁位移激发造成了FeⅡ的奇异核磁共振线形. 关键词：