C2H4的微波场助气相光催化氧化

用溶胶-凝胶法制备了多孔性TiO     

FTIR-ATR技术考察TiO2膜对油酸的光催化氧化性能

采用Sol-Gel和PVD法在玻璃、陶瓷、铝片表面制备出TiO2膜,直接将食用油中的主成分油酸用溶剂稀释后均匀涂在膜表面,采用FTIR-ATR技术实现了对膜样品光催化自清洁性能的快速准确评价,并通过测量水的接触角评价了膜的亲水性。结果表明,Sol-Gel法和PVD法制备的TiO2/玻璃膜都具有较好的光致亲水性和光催化降解油酸性能,两者的亲水性没有明显差别,但前者的光催化活性稍优于后者。比较Sol-Gel法制备的TiO2/玻璃、TiO2/陶瓷和TiO2/铝片膜对油酸的光催化降解性能发现,光照3·5h后3个样品的降解率分别为92%,85%和46%,表明基底材料性质对TiO2膜的光催化活性有明显影响,镀在非导电性玻璃和陶瓷表面的TiO2膜比镀在导电性金属铝表面的TiO2膜对油酸有更高的光催化降解能力。     

乙烯在纳米催化剂InVO4-TiO2上的可见光降解

The InVO₄-TiO₂ nano-crystalline photocatalyst was prepared by sol-gel method and characterized by DRS, FTIR, Raman and XRD. The photocatalytic activities of the prepared sample were investigated by photocatalytic degradation of ethylene in the gaseous phase under visible light irradiation (λ>450 nm). The results indicate that both of pure TiO₂ and InVO₄ or their simple mixture show no photocatalytic activities for degradation of ethylene under visible light irradiation. However, as-synthesized InVO₄-TiO₂ catalyzes the degradation of ethylene into CO₂ under visible light irradiation. In addition, the interaction between InVO₄ and TiO₂ results in some structural distortion to all the crystal forms of TiO₂ in as-synthesized catalyst InVO₄-TiO₂.     

形态结构和光电特性对纳米TiO2光催化性能的影响

采用sol-gel法制备了系列纳米TiO2光催化剂,运用X射线衍射、BET比表面测定、紫外漫反射吸收光谱和表面光电压谱等手段对催化剂进行表征,并以乙烯作为光催化反应的指标反应分子,研究了TiO2纳米晶的性质对于光催化活性的影响.随着焙烧温度的升高,TiO2的晶粒逐渐增大,比表面积下降,晶相由锐钛矿向金红石转变,其吸收带边与光伏响应阈值向长波方向移动,氧化－还原能力降低,降解乙烯的转化率迅速下降.     

原位红外光谱法研究La/TiO2对有机污染物的光催化降解

本工作采用改进的溶胶-凝胶法和浸渍法制备了TiO₂掺杂稀土离子La³⁺的La/TiO₂光催化剂，运用XRD、N₂吸附脱附、紫外可见漫反射光谱(DRS)、表面光电压谱(SPS)等手段进行表征，同时利用原位红外技术考察了La/TiO₂样品光催化降解乙烯、丙酮、苯的气-固相光催化氧化反应，对其光催化降解有机污染物的过程进行了研究。结果表明，TiO₂经适量La³⁺掺杂后，锐钛矿晶型的含量增加，晶粒度减小，比表面积增大，禁带宽度增加，表面光电压信号增强，光生电子-空穴对有效分离；La/TiO₂样品对乙烯、丙酮、苯的光催化性能与纯TiO₂相比均有不同程度的改善，乙烯可以被光催化氧化完全矿化生成CO₂，而丙酮被光催化氧化可能生成中间产物丙酸，苯被光催化氧化可能生成中间产物苯酚和苯醌。     

单分散纳米InVO4(正交相)的低温合成

InVO₄ is a new developed visible light responding photocatalyst for water decomposition, which is obtained by a solid-state reaction at high temperature traditionally. In this paper, pure InVO₄ nano-crystalline powder has been prepared by a hydrothermal process at low temperature and was characterized by TEM, IR, and X-ray diffraction. Many factors such as pH value, reaction time and temperature have been investigated. It is found that the optimal conditions for the preparation is: n_InCl3∶n_NaVO3=1∶2; temperature : 150 ℃; Reaction time: 4～8 h; pH=7.9～8.0. And the experimental result shows that it is a convenient way to get single dispersing InVO₄ nano-crystalline powder by flux in alkyl alcohol.     

沸石分子筛表面烷基锡接枝反应的研究

介绍表面金属有机化学方法改性沸石分子筛的研究概况，简要总结了近年来国内外对某些重要的分子筛（如，Y型沸石，镓磷沸石，丝光沸石，MCM－41）表面接枝烷基锡的研究成果，参考文献32篇。     

掺杂TiO2光催化膜材料的制备及其灭菌机理

采用sol-gel技术制备了掺杂TiO2膜,考察了制备条件对溶胶稳定性的影响,并从TiO2光催化反应的角度分析了膜功能材料的灭菌机理.结果表明,溶胶化过程中温度对掺杂胶体形成速度及胶体粒径分布影响很大,40℃时制备周期短,胶体稳定.TiO2膜材料的灭菌本质在于其光照激活后产生的自由基OH·和O-2·直接攻击细菌的细胞,致使细菌蛋白质变异或脂类分解,从而杀灭细菌并使之分解.TiO2膜功能材料的灭菌效果与TiO2晶相组成直接相关,其灭菌率随膜层中锐钛矿含量的增加而提高.     

四甲基锡在MCM-41分子筛表面的接枝反应及产物性能

研究了真空条件下SnMe4在MCM-41分子筛表面的接枝反应，并用元素分析、ICP、GC-MS、XRD、FTIR、DRS、13C及119Sn MAS NMR、XPS、BET、TPD、TPR等方法对产物的组成、结构和性质进行了表征.结果表明, 两者可以定量地进行化学反应，将确定数目的甲基锡基团接枝在分子筛表面, 形成SnMe3/MCM-41物种；接枝反应发生在分子筛表面上, 不破坏MCM-41分子筛骨架结构；改性分子筛的BET比表面积有所降低，孔体积变小, 表面性质发生变化.四甲基锡在MCM-41上接枝反应的温度为343 K,比它与HY沸石的反应温度(193 K)高得多，并且产物SnMe3/MCM-41的热稳定性也高于SnMe3/HY.     

芥子气模拟剂2-氯乙基乙基硫醚的光催化降解

利用连续流动微反、原位红外和GC/MS等手段考察了芥子气模拟剂2-氯乙基乙基硫醚（2-CEES）在P25 TiO2上的光催化降解反应,证实CO2和H2O是这个反应的最终产物.详细的跟踪分析表明,除了CO2和H2O外,在反应的气相混合物中可检测到C2H4、CH3CHO、CH4、CO、HCl和H2S；少量小分子的羧酸、醚和砜；微量C2H5SC2H5、C2H5S2C2H5、C2H5SC2H4Cl和CH2ClCH2Cl等中间产物;在反应后的催化剂表面可检测到C2H5S2C2H5、C2H5SC2H4OH、C4H9S2C2H5和C2H5S2C2H4OH、等物.根据这些结果提出了2-CEES光催化降解的反应机理,推断2-CEES的光催化降解涉及脱氯、C－S键断裂、有机硫化物光聚合和裂解等复杂过程最终转化为CO2和H2O.认为各种硫物种在表面的积聚引起了催化剂的缓慢失活.