Behaviour of Self-Standing CVD Diamond Film with Different Dominant Crystalline Surfaces in Thermal-Iron Plate Polishing

Self-standing CVD diamond films with different dominant crystalline surfaces are polished by the thermal-iron plate polishing method. The influence of the dominant crystalline surfaces on polishing etfficiency is investigated by measuring the removal rate and final roughness. The smallest rms roughness of 0.14 μm is measured with smallest removal rate in the films with the initial （220） dominant crystalline surface. Activation energy for the polishing is analysed by the Arrhenius relation. It is found that the values are 170kJ/mol, 222kJ/mol and 214kJ/mol for the film with three different dominant crystalline surfaces. Based on these values, the polishing cause is regarded as the graphitization-controlling process. In the experiment, we find that transformation of the dominant crystalline surfaces from （111） to （220） always appears in the polishing process when we polish the （111） dominant surface.     

直流电弧等离子体喷射化学气相沉积高质量金刚石膜残余应力分布的拉曼谱分析

不同工艺条件下在钼衬底(φ60mrn)上用100kW直流电弧等离子体喷射化学气相沉积设备进行金刚石膜的制备。金刚石膜用扫描电镜(SEM)、拉曼谱(激光激发波长为488m)和X射线衍射来表征。研究结果表明，在直流电弧等离子体喷射化学气相沉积金刚石膜的过程中，内应力大小从金刚石膜的中央到边缘是增加的，并且应力形式是压应力。这说明了在金刚石膜中存在明显的应力不均。甲烷浓度和衬底温度都影响金刚石膜中的内应力。随着甲烷浓度和衬底温度的提高，金刚石膜中的内应力呈增加的趋势。     

用有限元模拟的方法研究大面积自支撑金刚石膜沉积过程中的热应力

建立了没有过渡层和有过渡层的有限元模型,对大面积自支撑金刚石膜沉积过程中的热应力进行了研究.分别计算了在常用金属材料钼、钨、镍作衬底和用镀有钛过渡层的钼作衬底的情况下,膜/衬底间的热应力分布情况.模拟与实验的结果表明,在大面积自支撑金刚石膜沉积过程中,采用镀有钛过渡层的钼作衬底有利于热应力的释放,从而可能制备出高质量的大面积无裂纹金刚石膜.     

直流等离子体喷射制备无裂纹自支撑金刚石膜体的晶体组织设计

在自支撑金刚石膜体中发现网状、河流状和环状三种裂纹形式,这几种裂纹形式依沉积温度不同而不同.首次采用了原子力显微镜分析了金刚石自支撑膜体裂纹断裂机制,发现了穿晶断裂和沿晶断裂两种机制,其中,在网状裂纹中,穿晶断裂机制占主要地位;环状裂纹中,沿晶断裂机制占主要地位,而河流状裂纹是两种机制的混合.对应X射线衍射结果,(111)晶面占优的膜体易于开启穿晶断裂机制,(220)晶面占优的膜体易于开启沿晶断裂机制.使用Raman 谱测试的膜体中的本征应力在几十到几百MPa之间,且在膜体中存在应力剖面分布.Raman谱的结果还显示低缺陷的膜体组织有利于阻挡裂纹扩展.通过建立简单力学分析模型,推测了膜体组织对断裂强度的作用.根据实验结果和力学模型,制备了最厚2mm、最大直径120mm的无裂纹自支撑金刚石膜.     

Induced Nucleation of Diamond Films on ZnS Substrates Precoated with Ceramic Interlayer

We attempt to coat a multi-spectrum chemical-vapour-deposition ZnS substrate with smooth crystalline diamond films on the top of properly designed ceramic interlayer,which provides protection for ZnS against corrosion by the H2-CH4 microwave plasma and mitigates the thermal expansion coefficient mismatching between diamond and ZnS.However,difficulties in the homogeneous diamond nucleation on a ceramic interlayer were encountered.It was found that high rate nucleation of diamond could be induced by a metal or semiconductor mask placed on the top of ZnS.     

采用DC Arc Plasma Jet CVD方法沉积微/纳米复合自支撑金刚石膜

在30kW级直流电弧等离子体喷射化学气相沉积(DC Arc P lasm a Jet CVD)设备上,采用Ar-H2-CH4混合气体,通过调节甲烷浓度以及控制其他沉积参数,在Mo衬底上沉积出微/纳米复合自支撑金刚石膜。实验表明,当微米金刚石膜层沉积结束后,在随后的沉积中,随着甲烷浓度的增加,金刚石膜表面的晶粒大小是逐渐减小的。当甲烷浓度达到20%以上时,金刚石膜生长面晶粒呈现菜花状的小晶团,膜体侧面已经没有了粗大的柱状晶,而是呈现出光滑的断口,对该层进行拉曼谱分析显示,位于1145 cm-1附近有一定强度的散射峰出现。这说明所沉积的晶粒全部变为纳米级尺寸。     

微纳米复合金刚石自支撑膜的制备及微观结构的研究

在30 kW级直流电弧等离子喷射化学气相沉积装置下,采用Ar-H2-CH4混合气体,通过控制工艺参数,在多晶钼衬底上制备了微纳米复合多层金刚石自支撑膜.采用拉曼光谱对其进行成份分析、SEM观察膜体表面形貌,采用聚焦离子束(FIB)技术对其进行原位刻蚀,用高分辨电镜观察对其进行微观表征.结果显示,同普通微米膜相比,多层膜体是由微米晶金刚石层和纳米晶金刚石层组成,表面光滑,微米层与纳米层间具有相互嵌套式的界面,微/纳米复合多层金刚石自支撑膜中包含有纳米级金刚石晶粒、微米级金刚石晶粒和无定形碳.     

加氮对直流电弧等离子体喷射金刚石膜生长、形貌和质量的影响

利用直流等离子体喷射化学气相沉积法制备掺氮的金刚石厚膜.本文研究了在甲烷/氩气/氢气中加入氮气对金刚石膜生长、形貌和质量的影响.反应气体的比例由质量流量计控制,在固定氢气(5000sccm)、氩气(3000sccm)、甲烷(100sccm)流量的情况下改变氮气的流量,即反应气体中氮原子和碳原子的变化比例(N/ C比)范围是从0.06到0.68.同时金刚石膜在固定的腔体压力(4kPa)和衬底温度(800℃)下生长.金刚石膜用扫描电镜(SEM)、拉曼谱和X射线衍射表征.结果表明,氮气在反应气体中的大量加入对直流等离子体喷射制备金刚石膜的形貌、生长速率、晶体取向、成核密度等有非常显著的影响.     

硬质合金金刚石涂层工具基体真空渗硼预处理技术研究

研究了真空渗硼预处理硬质合金基体的表面组织、形貌、粗糙度,并在处理过的硬质合金基体上,用强电流直流伸展电弧等离子体CVD法沉积金刚石薄膜涂层.结果表明,真空渗硼预处理不仅可以有效地消除或控制钴在金刚石沉积时的不利影响,而且还显著粗化硬质合金基体表面.因此,提高了金刚石薄膜的质量和涂层的附着力,其临界载荷值达到1500N.     

直流电弧等离子体喷射化学气相沉积高质量金刚石膜残余应力分布的垃曼谱分析

不同工艺条件下在钼衬底(φ60mm)上用100 kW直流电弧等离子体喷射化学气相沉积设备进行金刚石膜的制备.金刚石膜用扫描电镜(SEM)、拉曼谱(激光激发波长为488nm)和X射线衍射来表征.研究结果表明,在直流电弧等离子体喷射化学气相沉积金刚石膜的过程中,内应力大小从金刚石膜的中央到边缘是增加的,并且应力形式是压应力.这说明了在金刚石膜中存在明显的应力不均.甲烷浓度和衬底温度都影响金刚石膜中的内应力.随着甲烷浓度和衬底温度的提高,金刚石膜中的内应力呈增加的趋势.