Preparation and characterization of silica—polyimide composite membranes coated on porous tubes for CO2 separation

Silica-polyimide microcomposite membranes were prepared on γ-alumina-coated α-alumina support tubes, and their gas permeation properties were evaluated with He, N₂ and CO₂. Smoothing of the substrate surface and hybridization of silica and polyamic acid were both effective to form defect-free thin composite membranes. The CO₂ permeance of a membrane with a silica content of 68 wt% was one order of magnitude higher than that of a polyimide membrane having the same thickness. The permselectivity of CO₂ to N₂ was 30 at 30°C and 13 at 100°C. Contributions of the silica and polyimide phases to permeance of the composite membrane were analyzed with a two-phase permeation model. The effective thickness of the rate-controlling polyimide phase was less than one-tenth of the total thickness of the silica-polyimide membrane.     

Tuning of luminescence spectra of neutral ruthenium(II) complexes by crystal waters

Neutral ruthenium(II) complexes [RuLL'(CN)2] (L, L' = bpy, dmb, dbb; bpy = 2,2'-bipyridine, dmb = 4,4'-dimethyl-2,2'-bipyridine, dbb = 4,4'-tert-butyl-2,2'-bipyridine) were prepared, and the luminescence characteristics of the complexes in the solid state were measured. The luminescence was tuned by crystal waters included in the crystals; for example, [Ru(dbb)2(CN)2] x 2H2O, [Ru(dbb)2(CN)2] x H2O, and [Ru(dbb)2(CN)2] emit luminescence at 640, 685, and 740 nm, respectively.     

Magnetic structure of graphite ribbon

Anoble mechanism of spin polarization is proposed for finite graphite sheet with edge. For graphite ribbon with zigzag edge, there appear peculiar ‘edge states’. These localized states comprise nearly flat band at the Fermi level, which easily causes magnetic instability. Magnetic structure is suggested from Hartree-Fock analysis of the Hubbard model, where huge magnetic moments are induced at around both of edges by weak HubbardU and are coupled antiferromagnetically with each other.     

Synthesis of 4-fluorinated UDP-MurNAc pentapeptide as an inhibitor of bacterial growth

4-Fluorinated UDP-MurNAc pentapeptide, 2, has been synthesized. In our previous study, UDP-MurNAc pentapeptide analogue 1 was found to be incorporated into the bacterial cell wall through biosynthesis. Compound 2 showed growth-inhibition activity against Gram-positive bacteria when it was added to growth media at 0.01 mg/mL. [structure--see text]     

Preparation and characterization of novel branched beta-cyclodextrins having beta-D-galactose residues on the non-reducing terminal of the side chains and their specific interactions with peanut (Arachis hypogaea) agglutinin

Six novel branched beta-cyclodextrins (betaCDs) having beta-D-galactose residues on the non-reducing terminal of the sugar side chains, namely 6(1),6(4)-di-O-(beta-D-galactosyl)-betaCD (10), 6-O-(beta-D-galactosyl)-betaCD (11), 6(1),6(4)-di-O-(beta-lactosyl)-betaCD (14), 6-O-(beta-lactosyl)-betaCD (15), 6(1),6(4)-di-O-(4'-O-beta-D-galactosyl-beta-lactosyl)-betaCD (18), and 6-O-(4'-O-beta-D-galactosyl-beta-lactosyl)-betaCD (19), were chemically synthesized using the trichloroacetimidate method. The reaction products were separated by HPLC on an amino column into dibranched and monobranched betaCDs. Their structures were confirmed by mass spectrometry (MS) and two-dimensional (2D) NMR spectroscopic analysis. To study the length of the sugar side chains attached to the CD ring, which leads to differences in the functions of the branched CDs, interactions of these compounds with peanut (Arachis hypogaea) agglutinin (PNA) were investigated using an optical biosensor and an inhibition assay based on hemagglutination. The results showed that all branched betaCDs interacted with PNA, and the binding affinity was 18>14>10 and 19>15>11 when the derivatives were compared on the basis of side chain length.     

A practical synthesis of (S)-2-cyclohexyl-2-phenylglycolic acid via organocatalytic asymmetric construction of a tetrasubstituted carbon center

[reaction: see text] A concise and enantioselective synthesis of (S)-2-cyclohexyl-2-phenylglycolic acid as a key intermediate for (S)-oxybutynin is reported. The crucial asymmetric tetrasubstituted carbon center was constructed with excellent stereoselectivity through the proline-catalyzed direct asymmetric aldol reaction between cyclohexanone and ethyl phenylglyoxylate under mild conditions.     

Thermal decomposition of the solvent-extracted chloro complexes of vanadium(IV) with trioctylamine and trioctylmethylammonium chloride

The complexes (R₃NHVO(OH)Cl₂)₂ and (R₃RNVO(OH)Cl₂)₂ prepared by drying in vacuo the organic solutions from the extraction into benzene of aqueous vanadyl chloride solution with trioctylamine (TOA, R₃N) and trioctylmethylammonium chloride (TOMAC, R₃RNCl), were studied by thermogravimetry and differential thermal analysis under an atmosphere of nitrogen, and the products of their thermal decomposition, such as volatile matter and residues, by gas chromatography. X-ray diffraction and infrared spectroscopy. It was found that the complexes with TOA and TOMAC thermally decompose to V₂O₃ at 200–300° by cracking of the compounds R₃NHVO(OH)Cl₂ and R₃RNVO(OH)Cl₂ formed via dissociation of the complexes at about 150°.

---

Zusammenfassung Die Komplexe (R₃NHVO(OH)Cl₂)₂ und (R₃RNVO(OH)Cl₂)₂ wurden hergestellt, indem benzolische und wässrige Vanadylchlorid-Lösungen mit Trioctylamin (TOA, R₃N) und Trioctylmethylammoniumchlorid (TOMAC, R₃RNCl) extrahiert und die erhaltenen Lösungen im Vakuum eingedampft wurden. Die Komplexen wurden in Stickstoffatmosphäre mittels TG und DTA untersucht und die thermischen Zersetzungsprodukte, und zwar sowohl die flüchtigen Verbindungen als auch die Rückstände, gaschromatographisch bzw. röntgendiffraktometrisch und IR-spektroskopisch bestimmt. Es wurde festgestellt, daß die Komplexe mit TOA und TOMAC bei 150° in die Verbindungen R₃NHVO(OH)Cl₂ und R₃RNVO(OH)Cl₂ dissoziieren, die bei 200–300° thermisch zu V₂O₃ zersetzt werden.

---

(R₃NHVO(OH)Cl₂)₂ (R₃RNVO(OH)Cl₂)₂ (R₃,) ( , R₃RNCl). , , . , 200–300° V₂₃ R₃NV()l₂ R₃RNVO(OH)Cl₂, 150°.

---

---

We wish to thank the Koei Chemical Co. Ltd. for samples of TOA and TOMAC.     

Absorption Spectra of Sodium Aluminate Solutions

The absorption spectra of sodium aluminate solutions have been examined at different concentrations. As a result, it was found that the characteristic absorption band due to aluminate ion shows a λ_max at 265–270 mm?.     

Pore size control and gas permeation kinetics of silica membranes by pyrolysis of phenyl-substituted ethoxysilanes with cross-flow through a porous support wall

A silica membrane was produced by chemical vapor deposition using tetraethoxysilane (TEOS), phenyltriethoxysilane (PTES) or diphenyldiethoxysilane (DPDES) as the Si source. Amorphous silica was deposited in the mesopores of a γ-alumina film coated on a porous -alumina tube, by evacuating the reactant through the porous wall. Hydrogen permeance at a permeation temperature of 600°C was of the order of 10⁻⁷ mol m⁻² s⁻¹ Pa⁻¹, and was not greatly dependent on the Si sources. The silica membrane produced using TEOS contained micropores permeable to both helium and hydrogen, but CO₂ and larger molecules were only slightly permeated through those mesopores which were left unplugged. The silica membrane produced from DPDES showed a single-component CO₂ permeance equivalent to that of single-component He, and CO₂/N₂ selectivity was approximately 9 at a permeation temperature of 30°C. When a mixture of CO₂ and N₂ was fed, however, CO₂ permeance decreased to the level of N₂ permeance. The H₂/N₂ selectivity, determined from single-component permeances to H₂ and N₂, was approximately 100, and these permeances remained unchanged when an equimolar mixture of H₂ and N₂ was fed. Thus, the DPDES-derived membrane possessed two types of micropores, abundant pores through which helium and hydrogen permeated and a small number of pores in which molecules of CO₂ and N₂ were permeable but not able to pass one another. Neither meso or macropores remained in the DPDES membrane.