Low-temperature suspension polymerization of vinyl pivalate for the preparation of syndiotacticity-rich ultrahigh molecular weight poly(vinyl alcohol) microfibrils with high yield

To prepare ultrahigh molecular weight (UHMW) poly(vinyl pivalate) (PVPi) with high conversion and high linearity for a precursor of syndiotacticity-rich UHMW poly(vinyl alcohol) (PVA), vinyl pivalate (VPi) was suspension polymerized using a low-temperature initiator, 2,2'-azobis(2,4-dimethylvaleronitrile) (ADMVN), and the effects of polymerization conditions on the polymerization behavior and molecular structures of PVPi and PVA prepared by saponifying PVPi were investigated. Suspension polymerization was slightly inferior to bulk polymerization in increasing the molecular weight of PVA. In contrast, the former was superior in increasing the conversion of the polymer. Suspension polymerization of VPi at 25 °C by controlling various polymerization factors proved to be successful in obtaining PVA of UHMW (number-average degree of polymerization (P_n): 14,700-16,700), high syndiotactic diad content (62%), and of high yield (ultimate conversion of VPi into PVPi: 85-90%). In the case of bulk polymerization of VPi under the same conditions, maximum P_n, conversion of 15,800-17,000, and 25-35% were obtained, respectively. The degree of branching was lower and the P_n and syndiotacticity were higher with PVA prepared from PVPi polymerized at lower temperatures. All PVAs from PVPi suspension-polymerized at 25 °C were fibrous, with a high degree of crystallinity and orientation of the crystallites.     

Preparation of water‐soluble,syndiotacticity‐rich,low molecular weight poly(vinyl alcohol) microfibrils in high yields with the low‐temperature polymerization of vinyl pivalate in tetrahydrofuran and saponification

To prepare water‐soluble, syndiotacticity‐rich poly(vinyl alcohol) (PVA) microfibrils for various industrial applications, we synthesized syndiotacticity‐rich, low molecular weight PVA by the solution polymerization of vinyl pivalate (VPi) in tetrahydrofuran (THF) at low temperatures with 2,2′‐azobis(2,4‐dimethylvaleronitrile) (ADMVN) as an initiator and successive saponification of poly(vinyl pivalate) (PVPi). Effects of the initiator and monomer concentrations and the polymerization temperature were investigated in terms of the polymerization behaviors and molecular structures of PVPi and the corresponding syndiotacticity‐rich PVA. The polymerization rate of VPi in THF was proportional to the 0.91 power of the ADMVN concentration, indicating the heterogeneous nature of THF polymerization. The low‐temperature solution polymerization of VPi in THF with ADMVN proved to be successful in obtaining water‐soluble PVA with a number‐average degree of polymerization (P_n) of 300–900, a syndiotactic dyad content of 60–63%, and an ultimate conversion of VPi into PVPi of over 75%. Despite the low molecular weight of PVA with P_n = 800, water‐soluble PVA microfibrillar fibers were prepared because of the high level of syndiotacticity. In contrast, for PVA with P_n = 330, shapeless and globular morphologies were observed, indicating that molecular weight has an important role in the in situ fibrillation of syndiotacticity‐rich PVA. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1103–1111, 2002     

Characterization of Nitro-Substituted Polybenzimidazole Synthesized by the Reaction with Nitric Acid

Abstract

Nitro-substituted poly[2,2′-(m-phenylene)-5,5′-bibenzimidazole]s (PBIs) were synthesized by the reaction of PBI with nitric acid in sulfuric acid under various conditions. The number of nitro groups substituted on the aromatic ring of PBI per polymeric unit varied from 1.44 to 3.55 according to the reaction conditions. An increase in reaction temperature and concentration of the nitric acid increased the degree of substitution. The inherent viscosity of the substituted polymer increased as the reaction temperature decreased. When the reaction temperature was 30°C, the inherent viscosity of the polymer increased as the concentration of nitric acid increased. The nitro-substituted PBI exhibited polyelectrolyte behavior in formic acid. The nitro groups substituted on PBI were dissociated when the polymer was heated to 450°C, displaying exothermic behavior, and the decomposition of polymer was proportional to its nitro group content. All nitro-substituted PBIs showed better solubilities in polar aprotic and acidic solvents, such as dimethylacetamide, dimethylsulfoxide, dimethylformamide, N-methylpyrrolidone, formic acid, sulfuric acid, and trifluoromethanesulfonic acid.     

In situ‐generated Ru(III)‐mediated ATRP from the polymeric Ru(III) complex in the absence of activator generation agents

Past research has examined the atom transfer radical polymerization (ATRP) with high oxidation state metal complexes and without the need for any additives such as reducing agent or free radical initiator. To extend this research, half‐metallocene ruthenium(III) (Ru(III)) catalysts were used for the polymerization of methyl methacrylate (MMA) for the first time. These catalysts were generated in situ simply by mixing phosphorus‐containing ligand and pentamethylcyclopentadienyl (Cp*) Ru(III) polymer ((Cp*RuCl₂)_n). The complexes in their higher oxidation state such as Cp*RuCl₂(PPh₃) were air‐stable, highly active, and removable catalysts for the ATRPs of MMA with both precision control of molecular weight and narrow polydispersity index. The addition of ppm amount of metal catalyst contributed to the formation of very well‐defined homopolymers and copolymers. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

2‐[(Diphenylphosphino)methyl]pyridine as ligand for iron‐based atom transfer radical polymerization

2‐[(Diphenylphosphino)methyl]pyridine (DPPMP) was successfully used as a bidentate ligand in the iron‐mediated atom transfer radical polymerization (ATRP) of methyl methacrylate (MMA) with various initiators and solvents. The effect of the catalytic system on ATRP was studied systematically. Most of the polymerizations with DPPMP ligand were well controlled with a linear increase in the number‐average molecular weights (M_n) versus conversion and relatively low molecular weight distributions (M_w/M_n = 1.10–1.3) being observed throughout the reactions, and the measured molecular weights matched the predicted values. Initially added iron(III) bromide improved the controllability of the polymerization reactions in terms of molecular weight control. The ratio of ligand to metal influenced the controllability of ATRP system, and the optimum ratio was found to be 2:1. It was shown that ATRP of MMA with FeX₂/DPPMP catalytic system (X = Cl, Br) initiated by 2‐bromopropionitrile (BPN) was controlled more effectively in toluene than in polar solvents. The rate of polymerization increased with increasing the polymerization temperature and the apparent activation energy was calculated to be 56.7 KJ mol^?1. In addition, reverse ATRP of MMA was able to be successfully carried out using AIBN in toluene at 80 °C. Polymerization of styrene (St) was found to be controlled well by using the PEBr/FeBr₂/DPPMP system in DMF at 110 °C. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 2922–2935, 2008     

Miscible blends of nitro‐substituted polybenzimidazole and polyetherimide

A novel blend system was prepared by blending organosoluble nitro‐substituted polybenzimidazole (NO₂‐PBI) and polyetherimide (PEI) in a cosolvent at a moderate condition. It was shown that the NO₂‐PBI/PEI blends not only possess tractable processability owing to the enhanced solubility of NO₂‐PBI but also retain the desirable features of unmodified PBI/PEI blends. Apparent miscibility in the blends was observed and attributed to hydrogen‐bonding interactions between N? H groups in NO₂‐PBI and carbonyl groups in PEI. It was revealed that the NO₂‐PBI/PEI blends phase‐separate upon heating above the glass‐transition temperatures. The observed mixing of NO₂‐PBI and PEI in a molecular level, although sustainable only in the glassy region, was shown to lend synergy effects to the physical properties of the blends. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 1778–1783, 2001     

Phosphorus ligands for iron(III)‐mediated ATRP of styrene via generation of activators by monomer addition

Styrene polymerization via generation of activators by monomer addition (GAMA) for atom transfer radical polymerization (ATRP) has been examined extensively with bulk FeX₃ and FeX₂ at 110 °C in conjunction with various phosphorus‐bearing ligands. It was found that GAMA possesses advantages over normal ATRP. Most importantly, narrower polydispersity index (PDI) values were observed from the styrene polymerizations with Fe(III) over those with Fe(II). Every instance of 2‐(diphenylphosphino)‐N,N′‐dimethyl‐[1,1′‐biphenyl]‐2‐amine and 2‐(diphenylphosphino) pyridine with the Fe(III) system were controlled excellently without addition of any radical initiator or reducing agent additives. Initiator type was found to exert a significant factor to influence on the controllability of polymerization. The initiation of 1‐phenylethyl chloride and methyl‐2‐chloropropionate gave rise to formation of polymers with narrow PDI (1.05–1.20), whereas those from 1‐phenylethyl bromide increased to 1.35. The GAMA of bulk styrene exhibited the best performance in terms of both rate and controllability compared with toluene and anisole. Both formation of block copolymer from the macroinitiator and efficient perturbation of polymerization with 2,2,6,6‐tetramethylpiperidine 1‐oxyl provided firm evidence to support the living and radical characteristics for the GAMA of styrene. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 144–151, 2010     

Vinylic polymerization of Norbornenecarboxylic Acid Esters by Palladium Complexes

In recent years certain new technologies demand optically transparent high Tgpolymer materials.Some aliphatic polymers containing cyclic structure are in the marketalready and have been applied to manufacture various devices in optics industry.However,these polymers are usually of nonpolar character and their difficulties inadhesion and solubility in solvents limited their applicability in many technologies[1 ,2 ] .The polymerization of polar group-containing internal cyclic olefins by transit…     

Preparation of Polyacrylonitrile Microfibers Using Gelation and Phase Separation During the Solution Polymerization of Acrylonitrile

Polyacrylonitrile (PAN) microfibrils were prepared directly via the solution polymerization of acrylonitrile at specified ratios of controlling solvent dimethyl sulfoxide (DMSO) to non‐solvent tert‐butyl alcohol. At first, gel formation occurred due to the interaction between DMSO and the cyano groups of PAN. The microfibrillar structure was then formed through the phase separation of PAN molecules from the gel. It is shown that very small variations in the solvent/non‐solvent ratio facilitate a major change in the gelation and phase separation processes.