基于MOF (Cu)@biochar气凝胶的制备及其在缓释氮肥上的应用

以羧甲基纤维素(CMC)、明胶和MOF(Cu)@biochar为原料,采用简单有效的冷冻干燥方法制备了(CMC/Gelatin/MOF(Cu)@biochar)杂化气凝胶,并用傅里叶变换红外光谱(FT-IR)、热重分析(TG)、X射线粉末衍射(XRD)、扫描电镜(SEM)和X射线光电子能谱(XPS)技术对其进行了表征;研究了MOF(Cu)@biochar含量、pH和不同的盐水溶液对杂化气凝胶溶胀行为的影响;以该气凝胶负载氯化铵,制备了一种新型缓释肥料(SRF),并研究了含2%(wt)SRF的沙性土壤的保水能力;SRF在土壤中第30天的累积释放率为79.4%;肥料在土壤中释放符合非Fickian扩散和阳离子交换的协同作用机理。     

Event-triggered design for discrete-time nonlinear systems with control constraints

Nonlinear Dynamics - In order to solve the constrained-input problem and reduce the computing resources, a novel event-triggered optimal control method is proposed for a class of discrete-time...     

基于不确定控制理论的最优策略研究

本文在不确定理论的框架下,研究一类带背景状态变量的最优控制模型.在乐观值准则下,利用不确定动态规划的方法,证明了不确定最优性原则,得到最优性方程.作为应用,求解一个固定缴费(DC)型养老金的最优投资策略问题,在乐观值准则下,以工资变量为背景状态变量,建立养老金模型.通过求解不确定最优性方程得到最优投资策略和最优支付率.     

Acridone-Based Host Materials for Green Phosphorescent and Thermally Activated Delayed Fluorescent OLEDs with Low-Efficiency Roll-Offs

By linking the carbazole unit to the nitrogen atom of acridone through phenyl or pyridyl, two compounds, named 10-(4-(9H-carbazol-9-yl)phenyl)acridin-9(10H)-one (AC-Ph-Cz) and 10-(5-(9H-carbazol-9-yl)pyridin-2-yl)acridin-9(10H)-one (AC-Py-Cz) were designed and synthesized. These two materials, characterized with highly twisted and rigid structure, good thermal stability, and balanced carrier-transporting properties, were employed as host materials for green phosphorescent and thermally activated delayed fluorescent organic light-emitting diodes (OLEDs). The carbazole group, despite its small contribution to the highest occupied molecular orbitals (HOMOs) of these two materials, plays an essential role as an intramolecular host in energy delivering and improving the hole transporting ability of these two hosts. The incorporation of the electron-deficient pyridyl group as a linking group slightly improves the electron transporting capability of AC-Py-Cz. The green phosphorescent OLED (PhOLED) based on AC-Py-Cz exhibited excellent device performance with a turn-on voltage of 2.5 V, a maximum power efficiency and an external quantum efficiency (η_ext) of 89.8 lm W⁻¹ and 25.2 %, respectively, benefitting from the better charge-balancing ability of AC-Py-Cz host due to the presence of the pyridyl bridge. More importantly, all the devices based on these two hosts showed low efficiency roll-off at high brightness due to the suppressed non-radiative transition in the emitting layer. In particular, the AC-Py-Cz-hosted green PhOLED exhibited an efficiency roll-off of 1.6 % from the maximum next at a high brightness of 1000 cd m⁻² and a roll-off of 15.9 % at an extremely high brightness of 10000 cd m⁻². This study manifests that acridone-based host materials have great potential in fabricating OLEDs with low efficiency roll-off.     

Fabricating Dual-Atom Iron Catalysts for Efficient Oxygen Evolution Reaction: A Heteroatom Modulator Approach

Understanding the thermal aggregation behavior of metal atoms is important for the synthesis of supported metal clusters. Here, derived from a metal–organic framework encapsulating a trinuclear Fe^III₂Fe^II complex (denoted as Fe₃) within the channels, a well-defined nitrogen-doped carbon layer is fabricated as an ideal support for stabilizing the generated iron nanoclusters. Atomic replacement of Fe^II by other metal(II) ions (e.g., Zn^II/Co^II) via synthesizing isostructural trinuclear-complex precursors (Fe₂Zn/Fe₂Co), namely the “heteroatom modulator approach”, is inhibiting the aggregation of Fe atoms toward nanoclusters with formation of a stable iron dimer in an optimal metal–nitrogen moiety, clearly identified by direct transmission electron microscopy and X-ray absorption fine structure analysis. The supported iron dimer, serving as cooperative metal–metal site, acts as efficient oxygen evolution catalyst. Our findings offer an atomic insight to guide the future design of ultrasmall metal clusters bearing outstanding catalytic capabilities.     

利用沙漠沙低温合成高长径比莫来石晶须

利用沙漠沙独特的化学组成特性和矿物特性,将沙漠沙荒料作为硅源,工业Al(OH)3作为铝源制备莫来石晶须.改变硅源/铝源配比和合成温度,结合XRD、SEM、TEM研究莫来石生长环境和自由生长形态的变化.研究结果表明:当沙漠沙与Al(OH)3的质量比为35/65时,在1200℃的低温下就能获得平均值>60的高长径比莫来石晶须;随着煅烧温度的升高,莫来石晶须长径比不断增大,当温度升至1300℃,平均长径比>94.随着合成温度的升高,莫来石的形成经过了一次莫来石和二次莫来石化两个阶段;若配方中Al2 O3处于过饱和状态,样品中刚玉相会随着煅烧温度的升高出现先增多后降低的变化现象.     

四方体MgO的制备及对有机染料的吸附

以六水氯化镁和六次甲基四胺为原料,采用水热法合成四方体MgO,考察其对有机染料甲基橙和亚甲基蓝的吸附行为.通过TGA-DTA、SEM、XRD、N2-sorption和FT-IR等手段表征样品.结果表明,原料浓度、温度和表面活性剂对四方体MgO结构的形成影响较小,而反应时间的延长有助于有序结构的组装.温度170℃、时间24h、MgCl2·6H2O与C6H12N4浓度比为1∶2和表面活性剂PVP是制备四方体MgO的最佳条件.在溶液浓度10mg · L-1的单一吸附实验过程中,四方体MgO对甲基橙和亚甲基蓝的去除率分别为91.3;和22.3;,吸附过程均为单层吸附且符合Langmuir等温吸附模型和伪二级吸附动力学方程.在溶液浓度40 mg·L-1、甲基橙和亚甲基蓝浓度比3∶1的混合溶液吸附过程中,四方体MgO对甲基橙和亚甲基蓝的去除率分别为80.1;和97.9;.     

烧结温度对煤系高岭土制备堇青石陶瓷的影响

我国的煤系高岭土具有明显的资源优势,应对其进行充分地研究和合理地应用,以缓和优质高岭土资源枯竭的燃眉之急.以鄂尔多斯煤系高岭土、鄂尔多斯滑石、工业氧化铝为原料,通过反应烧结一步合成堇青石,探讨了堇青石合成温度范围,以拓宽该煤系高岭土的应用范围.通过高温显微镜观察堇青石试样的合成温度范围为1400～1420℃.经1420℃合成的堇青石试样的吸水率为16.11;,显气孔率为28.44;,体积密度为1.77 g/cm3,径向烧成收缩为1.77;,厚度烧成收缩为4.80;,抗折强度为43.56 MPa.镁铝尖晶石是合成堇青石的重要中间产物,适当提高烧结温度可以促进镁铝尖晶石相向堇青石相转变,有利于堇青石晶粒的生长与发育.烧结温度的变化是堇青石晶粒发生变化的原因,同时导致液相量的变化,最终影响堇青石试样显微结构和烧结性能.