钛酸酯偶联剂对包硅铝钛白粉表面的有机改性

The surface organic modification of TiO2 particles with titanate coupling reagent,which was pre-coated with double layers of SiO2 and Al2O3,was studied.Experiments showed that the modified particles exhibited hydrophobic characteristics.The modification state of the particle surface was characterized by IR spectroscopic measurement,pyrolytic gas chromatography,thermogravimetric analysis and X-ray photoelectron spectra.The titanate coupling reagent binding with the hydroxyl on the particle surface was analyzed.The surface characteristics of pre-modification and post-modification particles were compared.     

硅铝氧化物二元包覆钛白粉颗粒的有机改性

在二元包覆ＳiO2,AL2O3薄膜的基础上,用钛酸酯偶联剂、硅烷偶联剂及三乙醇胺、系戊四醇对亚微米ＴiO2颗粒表面进行有机改性,考察了改性条件对果粒表面改性结果的影响,通过疏水性试验和润湿试验对改性前后ＴiO２颗粒的表面特性进行了表征,高温裂解色谱、热重分析、Ｘ光电子能谱的测试结果表明,不同改性剂与颗粒表面存在不同程度的化学键合作用,分析了改性剂在粒表面的包覆状态与结构。     

液相沉积法制备TiO2颗粒表面包覆SiO2纳米膜

研究了用液相沉积法在TiO2颗粒表面包覆SiO2纳米膜的过程.通过透射电镜(TEM)和酸溶实验分析,证实本实验在TiO2颗粒表面包覆了一层连续、致密的SiO2纳米膜.ζ-电位分析表明,颗粒表面只需少量包覆就可以显著改变颗粒表面的电动力学行为.采用 X射线荧光光谱分析仪（XRF）测定SiO2包覆量随包覆过程的变化.通过X射线光电子能谱（XPS）分析,获得Ti 2p、Si 2p及 O 1s电子结合能及其相对强度随包覆过程的变化规律,揭示硅酸分子在TiO2颗粒表面的包覆过程.分析表明,初期形成的活性硅酸分子与TiO2颗粒表面的羟基反应形成Ti－O－Si键,后期形成的硅酸分子与已键合在表面的硅酸发生缩合反应,形成连续致密的硅膜,膜层在陈化过程中继续缓慢生长.