Thin film synthesis and the influence of irradiation-induced defects on the superconductivity of La1.8Sr0.2CuO4

Thin superconducting films of La_1.8Sr_0.2CuO₄ have been prepared by magnetron sputter deposition and subsequent temperature treatment. The composition of the films has been determined by Rutherford backscattering and the structure by thin film X-ray diffraction. The onset of superconductivity was about 32 K and the midpoint near 28 K. Defect production in the films by He ion bombardment revealed a drasticT _c reduction with a sensitivity similar to that observed in the Chevrel phases. Oxygen implantation and subsequent annealing led to an enhancement of theT _c onset.     

Superconducting and structural properties of YBaCuO thin films deposited by inverted cylindrical magnetron sputtering

Thin films of YBaCuO have been deposited onto Al₂O₃, MgO, SrTiO₃ and ZrO₂ substrates by inverted cylindrical magnetron sputtering. The main advantage of this preparation technique is the high reproducibility of the results allowing systematic studies of the film properties as a function of deposition parameters. Optimum preparation conditions were a low discharge voltage (100 V), a high oxygen partial pressure (2×10^–1 Torr) in an oxygen argon mixture, and substrate temperatures around 800°C. The films grow highly textured on all substrates yielding single crystalline growth on SrTiO₃ and MgO as proved by X-ray diffraction and channeling. The zero resistance values of the sharp transtions usually are around 90 K. highest critical current densities were determined in films grown on MgO and SrTiO₃ with values up to 5.5×10⁶ A/cm² at 77 K.