Crosslinked polystyrene with improved mechanical properties

The synthesis of some divinyl monomers—bis(vinylphenyl)ethane ( 2 ), bis(vinylbenzyloxy)hexane ( 3a ), and bis(vinylbenzyloxy)dodecane ( 3b ) is reported. Copolymers of the new monomers and styrene were evaluated as an alternative to divinylbenzene-crosslinked polymers for use as matrices and absorbents. The mechanical properties and the amount of residual double bonds in the copolymers were compared. It was found that the new copolymers, unlike the divinylbenzene-crosslinked polymers, retained their mechanical strength even at high crosslinking degrees. Stress at break values of 79, 68, and 18 N/mm² were found for the polymers crosslinked with 20 mol % of 3a, 2 , and divinylbenzene; 5, 25 and 45% of the divinyl units in these polymers were left as pendant double bonds. Porous styrene– 2 copolymers were synthesized and shown to have lower surface areas than the corresponding divinylbenzene-crosslinked polymers. The pore size distribution showed that this was due to the absence of the smallest pores which are found in the divinylbenzene-crosslinked polymers in between heavily crosslinked nodules. © 1993 John Wiley & Sons, Inc.     

Saturated heterocycles. 251 . Determination of σ+ values of heteroaryl-substituted phenyl groups via ring-chain tautomerism

The Hammett-Brown electrophilic substituent constants σ⁺ for five heteroaryl-substituted phenyl groups were estimated via the ring-chain tautomeric equilibria of three sets of oxazolidines and 1,3-oxazines in deuteriochloroform solution. For oxazolidines derived from norephedrine and norpseudoephedrine, the σ⁺ values were also determined via the gas-phase ring-chain equilibria, by means of mass spectrometry. The results show that the heteroaromatic substituents studied have a slight electron-withdrawing character, with σ⁺ in the range -0.03 to 0.59. The gas-phase σ⁺ values are significantly higher than the solution values.     

Pt coated Cr2O3 thin films for resistive gas sensors

The resistive response of atomic layer deposited thin epitaxial α-Cr₂O₃(0 0 1) films, to H₂ and CO in air, was studied. The films were covered with Pt nanoislands formed by electron-beam evaporation of a sub-monolayer amount of the material. The gas measurements were performed at 250°C and 450°C. These temperatures led to different proportion of chemical states, Pt²⁺ and Pt⁴⁺, to which the Pt oxidized. The modification was ascertained by the X-ray photoelectron spectroscopy method. As a result of the modification, the response was fast at 250°C, but slowed at 450°C. A disadvantageous abundance of Pt⁴⁺ arising at 450°C in air could be diminished by high-vacuum annealing thus restoring the response properties of the system at 250°C.      

Diagnostic performance of low field MRI in acute knee injuries

The diagnostic performance of low field (0.1 T) magnetic resonance imaging (MRI) was studied prospectively and double-blindly among 33 patients with acute knee injuries. The subsequent arthroscopy was the golden standard. For lesions of the medial meniscus low field MR had a sensitivity of 88% and a specificity of 80%; for lesions of the lateral meniscus the sensitivity was 25% and the specificity 97%. For anterior cruciate ligament tears, low field MRI had a sensitivity of 83% and a specificity of 85%. The specificity for posterior cruciate ligament tears was 97%. The performance of low field MRI equalled that reported earlier for high field MRI, the only exception being the sensitivity for lateral meniscus lesions.     

Carboxymethyl cellulose on a fiber substrate: the interactions with cationic polyelectrolytes

High and low molecular weight (M_w) carboxymethyl celluloses (CMC) were adsorbed on a well-characterized fiber substrate (long fibers of a commercial bleached birch kraft pulp with the carboxylic acid groups in Na-form) to increase the charge of the fibers in a controlled fashion. The M_w played a role in the utilization of CMCs as a strength additive in paper sheets nearly doubling the tensile strength with the high M_w CMC. Swelling properties of the CMC treated fibers were measured with water retention value (WRV). The WRV increased more with the high M_w CMC. The swelling was further tuned by two highly cationic polyelectrolytes; high M_w poly(diallyldimethyl ammonium chloride) (PDADMAC) and low M_w polybrene (hexadimethrine bromide, [3,6]-ionene). They were chosen because of their known ability to neutralize the anionic charge either exclusively on the surface or in the whole fiber, respectively. Adsorption of PDADMAC could reduce WRV of the CMC pre-treated fibers to the level of the untreated reference, while polybrene adsorbed pulps with 3–10 times more cationic polyelectrolyte deswelled the fibers only slightly more than the surface neutralized fibers. These results indicated surface conformation differences with low and high M_w CMCs. While the conformation did play a role after physical alteration (drying and rewetting) of the fibers, the paper sheets produced from these fibers showed remarkable differences. In extreme cases, the strength of the paper could be retained after drying (low M_w CMC + PDADMAC) or paper, resistant to disintegration, could be achieved (CMC + polybrene).