Transport properties and anomalous fatigue effect of Ag/Bi_(0.9)La_(0.1)FeO_3/La_(0.7)Sr_(0.3)MnO_3 heterostructures

The transport properties and fatigue effect of Ag/Bi0.9La0.1FeO3/La0.7Sr0.3MnO3 heterostructures are described. By examining the I–V curves, an anomalous fatigue effect was found and its influences on resistive states were studied. I–V curves combined with C– f spectra were used to directly analyze the transport properties and fatigue effect. Compared to the first I–V cycle state, this structure shows more than one order increase of resistance after 100 cycles of "I–V curve training". The redistribution of oxygen vacancies in the depletion layer of Ag/Bi0.9La0.1FeO3 is believed to be responsible for the different resistance mechanisms and tenfold magnitude drop in resistance. The resistive switching is understood to be caused by electric field–induced carrier trapping and detrapping, which changes the depletion layer thickness at the Ag/Bi0.9La0.1FeO3 interface.     

锆钛酸铅薄膜的溶胶-凝胶制备工艺及结构与物性的研究

采用溶胶-凝胶匀胶法制备锆钛酸铅铁电薄膜,研究了前驱体影响因素(如有机溶剂、前驱单体加入顺序、添加剂)、溶胶影响因素(如溶胶浓度、pH值)、匀胶速度和退火温度对成膜质量及薄膜微结构、铁电性的影响.结果表明:采用乙二醇甲醚为溶剂对pb2+、Zr4+和Ti4+金属盐进行溶解优于乙醇和乙二醇,但由于乙二醇甲醚对硝酸锆的溶解性差,对硝酸锆应先用乙醇溶解再加入乙二醇甲醚的方法来进行溶解;以硝酸锆为Zr源配制溶胶时,只有先将Pb前驱液滴加到Ti前驱液中,然后再滴入Zr前驱液的方式才能得到澄清前驱体.将锆钛酸铅溶胶浓度和pH值分别控制在0.2～0.3 mol/L和2～3较为适宜,与此溶胶相适应的匀胶参数:转速为4000 r/min,时间为60 s.随退火温度升高,薄膜的晶化程度增加,且逐渐表现出(100)晶面择优取向,晶格常数c和四方率c/a逐渐增加,而晶格常数a逐渐减小;随退火温度升高,晶粒尺寸逐渐增大,使得剩余极化强度逐渐增加,矫顽场强逐渐减小.当退火温度为850 ℃时制备的锆钛酸铅薄膜具有均匀的晶粒、较低的表面粗糙度和最为优异的铁电性.     

In2O3:H03+,Yb3+纳米晶的制备与上转换发光

以乙二醇为溶剂,采用低温溶剂热法制备了H03+/Yb3+共掺杂In2O3纳米晶.利用X射线晶体衍射 (XRD)、透射电子显微镜(TEM)对粒子的结构和形貌进行表征,结果表明,合成的样品为纯的立方相In2O3,颗粒尺寸约为30nm.通过上转换发光(UCL)光谱研究了粒子的上转换发光性质,在980nm半导体激光激 发下...     

微波烧结制备铁酸铋陶瓷的介电性和铁电性

采用微波烧结法制备铁酸铋多铁陶瓷,研究了微波烧结时间对其显微结构、介电性和铁电性的影响.结果表明:在4 kW下烧结35～40 min制备出基本为纯相的铁酸铋陶瓷;随烧结时间增加,铁酸铋陶瓷结构越来越致密,晶粒尺寸有一定程度增大;在-10～90℃范围内,介质损耗随烧结时间增加而增大;随微波烧结时间增加,剩余极化强度增大,而矫顽场强先增加后减小,且铁电性具有明显的频率依赖性;铁酸铋陶瓷的漏电流随微波烧结时间增加而减小,这是结构致密化的结果.     

In2O3:H03+,Yb3+纳米晶的制备与上转换发光

以乙二醇为溶剂,采用低温溶剂热法制备了H03+/Yb3+共掺杂In2O3纳米晶.利用X射线晶体衍射 (XRD)、透射电子显微镜(TEM)对粒子的结构和形貌进行表征,结果表明,合成的样品为纯的立方相In2O3,颗粒尺寸约为30nm.通过上转换发光(UCL)光谱研究了粒子的上转换发光性质,在980nm半导体激光激 发下,In2O3:H03+,Yb3+纳米晶发射出强的绿色和弱的红色上转换发光,分别归属于H03+离子(5 F4,5S2)→5I8 和5F5→5I8跃迁.研究了不同H03+和yb3+离子掺杂浓度对上转换发光性能的影响,确定了H03+和yb3+最 佳掺杂摩尔分数分别为3%和4%.双对数曲线显示,绿光和红光的发射过程均为双光子吸收过程.对样品 的上转换发光机制进行了初步讨论.     

基于主成分分析和BP神经网络的柑橘黄龙病诊断技术

柑橘黄龙病的传统诊断方法主要依赖于人眼经验及生化技术,前者凭经验,诊断快,但准确性低;后者准确性高,但效率低和成本高.本文采用高光谱成像技术,获取5种症状柑橘叶片的高光谱图像,采用基于主成分分析和BP神经网络相结合的方法,对370~988nm波段范围内的柑橘叶片高光谱图像进行了病状的无损检测.研究结果表明,柑橘叶片的高光谱图像存在很大冗余,前四个主成分累积方差贡献率达到97.42%.数据建模分类得表明:BP神经网络的分类准确率达85%以上,经主成分后再利用BP神经网络的分类准确率绝大部分达到90%以上.因此,利用高光谱成像技术进行柑橘黄龙病的早期诊断具有较高的可行性.     

绿色荧光体CaSe2O4:Ce3+的共沉淀合成与表征

以草酸为沉淀剂,用共沉淀法合成前驱体粉末,然后将前驱体粉末在5%H2+95%N2的还原气氛下煅烧,得到发光性能良好的CaSe2O4:Ce3+荧光粉.应用X射线粉末衍射(XRD)、荧光光谱(FS)、综合热分析(TC-DSC)和扫描电镜(SEM)等测试手段对前驱物及煅烧后的粉体进行表征.结果表明:烧结温度于800℃以上时,都町以得到正交结构的纯相CaSc2O4:Ce3+荧光体;其最大激发和发射波长分别在450和510 nm,与高温固相法所得产品的发射波长相同.荧光粉优化的合成条件为:Ce3+的最件掺杂浓度为1%(摩尔分数),最佳煅烧条件为1100℃煅烧6 h.最佳煅烧温度较传统的高温固相法(1600℃)低了约500℃,所得产品的发光强度接近高温固相法的产品.     

铟锡氧化物纳米粉体的低温溶剂热法制备

以氯化铟和氯化锡为原料,氨水为沉淀剂,先用化学沉淀法制备了前驱体,然后将该前驱体以乙二醇为溶剂在聚四氟乙烯内衬的反应釜中于低至190 ℃下反应,获得了铟锡氧化物(ITO)纳米粉体。采用扫描电子显微镜(SEM)、X射线衍射(XRD)及纳米粒度仪Zetasizer Nano-ZS对在不同温度、不同时间下反应的所得的ITO纳米粉体进行了表面形貌、结构和粒度分布等分析。结果表明,制备的ITO纳米粉体为立方晶相,粉体的平均颗粒小于100 nm;与已有的ITO纳米粉体制备方法相比,本溶剂热法制备过程无需高温烧结、流程简单,反应过程所需的温度可低至190 ℃,是迄今为止文献报导制备ITO的最低温度,同时所得产物纯度高、粒度均匀、分散性很好。