Degradation behavior of electrical properties of GaInAs (1.0 eV) and GaInAs (0.7 eV) sub-cells of IMM4J solar cells under1-MeV electron irradiation

In this work the degradation effects of the Ga_(0.7)In_(0.3)As(1.0 eV) and Ga_(0.42)In_(0.58)As(0.7 eV) sub-cells for IMM4J solar cells are investigated after 1-MeV electron irradiation by using spectral response and photoluminescence(PL) signal amplitude analysis, as well as electrical property measurements. The results show that, compared with the electrical properties of traditional single junction(SJ) GaAs(1.41 eV) solar cell, the electrical properties(such as Isc, Voc, and Pmax)of the newly sub-cells degrade similarly as a function of log ?, where ? represents the electron fluence. It is found that the degradation of Voc is much more than that of Isc in the irradiated Ga_(0.42)In_(0.58)As(0.7 eV) cells due to the additional intrinsic layer, leading to more serious damage to the space charge region. However, of the three types of SJ cells with the gap widths of 0.7, 1.0, and 1.4 eV, the electric properties of the Ga_(0.7)In_(0.3)As(1.0 eV) cell decrease largest under each irradiation fluence. Analysis on the spectral response indicates that the Jsc of the Ga_(0.7)In_(0.3)As(1.0 eV) cell also shows the most severe damage. The PL amplitude measurements qualitatively confirm that the degradation of the effective minority carrier life-time(τeff) in the SJ Ga_(0.7)In_(0.3)As cells is more drastic than that of SJ GaAs cells during the irradiation. Thus,the output current of Ga_(0.7)In_(0.3)As sub-cell should be controlled in the irradiated IMM4J cells.     

100 keV质子辐照对空间GaAs/Ge太阳电池光电效应的影响

利用空间环境模拟设备,用固定能量为100keV、注量为1×10⁹—3×10¹²cm^-2的质子,对空间实用GaAs/Ge太阳电池进行了辐照试验.利用伏安(I-V)特性、光谱响应和光致发光(PL)光谱测试,研究分析了电池的光电效应.试验表明,电池的各种电性能参数如短路电流(I_sc)、开路电压(V_oc)、最大输出功率(P_{m< 关键词： GaAs/Ge太阳电池 质子辐照 光电效应}