二氧化钛含量对铈稳定立方氧化锆陶瓷的性能影响

本文用无压烧结法成功制备了高硬度的立方氧化锆陶瓷,研究了氧化锆陶瓷的物相,Vickers硬度,显微结构,相对密度等性能,主要分析了TiO2添加量对Zr0.8Ce0.2O2陶瓷硬度和相对密度的影响。结果表明:烧结助剂TiO2可以有效抑制陶瓷晶粒异常生长,加快气孔排除,促进氧化锆陶瓷烧结致密化,提高陶瓷硬度。最高维氏硬度为20.2 GPa,最高相对密度达到了99.8%。     

Y2O3∶C陶瓷的发光性能

采用传统陶瓷制备工艺制备了C掺杂的Y₂O₃多晶陶瓷;研究了Y₂O₃∶C陶瓷的光谱性能,发现在403 nm有明显的发射峰。通过对其激发光谱的研究,表明它们是由F⁺和F色心造成的。本文还研究了Y₂O₃∶C陶瓷的热释光和光释光性能。用2个指数衰变函数拟合光衰变曲线得到的衰变时间常数τ₁=(4.66±0.27)s,τ₂=(23.31±1.03) s。     

Spectral and laser properties of Yb and Ho co-doped（YLa）2O3 transparent ceramic

Highly transparent Yb,Ho doped(YLa)2O3 ceramic was fabricated by conventional ceramic processing with nanopowders.The absorption and emission spectra of the ceramic was investigated.The energy transfer mechanism between Yb3+ and Ho3+ was also discussed.The strong emission band around 2 μm indicated that the Yb-Ho:(Y 0.90 La 0.10)2O3 transparent ceramic is a promising gain medium for the generation of 2 μm laser emissions.The laser operation of Yb-Ho co-doped(YLa)2O3 ceramic at 2.1 μm is first reported.     

α-Al_2O_3透明陶瓷的发光及热释光特性

采用传统无压烧结工艺,以MgO为烧结助剂,制备出了透明性良好的α-Al2O3透明多晶陶瓷,测定了其吸收光谱、荧光光谱、激发光谱,并做了热释光测试.结果表明,吸收光谱存在192nm和225—250nm吸收峰,分别对应于F色心和F+色心.在荧光光谱的410nm处发现有明显的发射峰.结合对其激发光谱的研究,证明了对应于F和F+色心.热释光谱中存在368,456,614K三个热释光峰,其中456K的峰值是受热激发的电子与F+色心复合产生的.     

不同粉料制备Nd∶(Y_(0.9)La_(0.1))_2O_3透明陶瓷及其性能

分别采用液相法和固相法制备的纳米粉,制得透明性良好的Nd∶(Y0.9La0.1)2O3透明陶瓷,并测试了各样品的结构,光谱及光学性能.结果表明:该陶瓷具有相同的光谱性能;但液相法复合纳米粉制备的透明陶瓷光学性能优于固相反应法制备的透明陶瓷;固相反应法制备的透明陶瓷,由于有部分La2O3分布不均,易导致晶粒生长不均匀和残留少量气孔;长时间球磨混料,也不利于样品性能的提高.     

Y2O3:C陶瓷的发光性能

采用传统陶瓷制备工艺制备了C掺杂的Y2O3多晶陶瓷;研究了Y2O3:C陶瓷的光谱性能,发现在403 nm有明显的发射峰.通过对其激发光谱的研究,表明它们是由F+和F色心造成的.本文还研究了Y2O3:C 陶瓷的热释光和光释光性能.用2个指数衰变函数拟合光衰变曲线得到的衰变时间常数τ1=(4.66±0.27)s,τ2=(23.31±1.03)s.     

La2O3对Yb3+掺杂的氧化钇透明激光陶瓷性能的影响

本文研究了La2O3的含量对(Yb0.05 Y0.95)2O3透明激光陶瓷的结构性能和烧结性能的影响.结果表明:随着La2O3含量的增加,拉曼光谱特征峰发生红移,声子能量降低,半高宽增大,相对强度先增大后减小;同时密度、相对密度和透过率都增大,陶瓷的晶粒减小,而当La2O3含量继续增加时,晶粒基本保持不变.但适量的La2O3掺杂量对(Yb0.05Y0.95)2O3透明激光陶瓷的发射性能影响不大.最合适的La2O3添加量为10at%,最合适的烧结温度为1700℃,最后样品的直线透过率可达到75%.     

The fluorescence and thermoluminescence characteristics of α-Al2O3:C ceramics

This paper reports that polycrystalline α-Al₂O₃:C ceramics are fabricated by conventional ceramics process. The excitation, emission spectra, thermoluminescence (TL) and optical stimulated luminescence (OSL) of α-Al₂O₃:C polycrystalline ceramics are investigated. There exists 410nm maximum emission peak which is caused by recombination of an electron with F⁺ centre to produce an excited F centre. The samples show three clear TL glow peaks at 405, 493 and 610K. The attenuation constant of exponentially decaying fast component (τ₁) and slow component(τ₂) of OSL curve are 8.43s and 41.73s, respectively. Those fluorescence and thermoluminescence characteristics are similar with α-Al₂O₃:C crystal.     

不同粉料制备Nd∶(Y0.9La0.1)2O3透明陶瓷及其性能

分别采用液相法和固相法制备的纳米粉,制得透明性良好的Nd∶(Y0.9La0.1)2O3透明陶瓷,并测试了各样品的结构,光谱及光学性能.结果表明:该陶瓷具有相同的光谱性能|但液相法复合纳米粉制备的透明陶瓷光学性能优于固相反应法制备的透明陶瓷|固相反应法制备的透明陶瓷,由于有部分La2O3分布不均,易导致晶粒生长不均匀和残留少量气孔|长时间球磨混料,也不利于样品性能的提高.