Growth of Semi-Insulating GaN Using N2 as Nucleation Layer Carrier Gas Combining with an Optimized Annealing Time

Semi-insulating （SI） GaN is grown using N2 as the nucleation layer （NL） carrier gas combined with an optimized annealing time by metalorganic chemical vapour deposition. Influence of using 1-12 and N2 as the NL carrier gas is investigated in our experiment. It is found that the sheet resistance of unintentionally doped GaN can be increased from 10^4 Ω/sq to 10^10 Ω/sq by changing the NL carrier gas from 1-12 to N2 while keeping the other growth parameters to be constant, however crystal quality and roughness of the tilm are degraded unambiguously. This situation can be improved by optimizing the NL annealing time. The high resistance of GaN grown on NL using N2 as the carrier gas is due to higher density of threading dislocations caused by the higher density of nucleation islands and small statistic diameter grain compared to the one using 1-12 as carrier gas. Annealing the NL for an optimized annealing time can decrease the density of threading dislocation and improve the tilm roughness and interface of AlGaN/GaN without degrading the sheet resistance of as-grown GaN signiticantly. High-quality SI GaN is grown after optimizing the annealing time, and AlGaN/GaN high electron mobility transistors are also prepared.     

AlGaN/AlN/GaN结构中二维电子气的输运特性

对使用金属有机物汽相沉积法生长的AlGaN/AlN/GaN结构进行的变温霍尔测量，测量结果指出在AlN/GaN界面处有二维电子气存在且迁移率和浓度在2K时分别达到了1.4×10⁴cm²·V^-1·s^-1和9.3×10¹²cm^-2，且在200K到2K范围内二维电子气的浓度基本不变，变磁场霍尔测量发现只有一种载流子(电子)参与导电.在2K温度下，观察到量子霍尔效应，Shubnikov-de Haas (SdH) 振荡在磁场约为3T时出现，证明了此结构呈现了典型的二维电子气行为.通过实验数据对二维电子气散射过程的半定量分析，推出量子散射时间为0.23ps，比以往报道的AlGaN/GaN结构中的散射时间长，说明引入AlN层可以有效减小合金散射，进一步的推断分析发现低温下以小角度散射占主导地位.     

Electroluminescence of an n-ZnO/p-GaN Heterojunction under Forward and Reverse Biases

Electroluminescent characteristics of n-ZnO/p-GaN heterojunctions under forward and reverse biases are studied. Emissions at 389nm and 57Ohm are observed under forward bias. An unusual emission at 390ram appears under reverse bias, and is attributed to the recombination in the p-GaN side of the heterojunction. The yellow emission peaked at 57Ohm is suppressed under reverse bias. The light intensity exponentially depends on the reverse current. The emission under reverse bias is correlated to tunnelling carrier transport in the heterostructure. Our results also support that the well-known yellow band of GaN comes from the transitions between some near-conduction-band-edge states and deep localized acceptor states.     

Growth of Semi-Insulating GaN by Using Two-Step AIN Buffer Layer

Semi-insulating GaN is grown by using a two-step A1N buffer layer by metalorganic chemical vapour deposition. The sheet resistance of as-grown semi-insulating GaN is dramatically increased to 10^13 Ω/sq by using two-step A1N buffer instead of the traditional low-temperature GaN buffer. The high sheet resistance of as-grown GaN over 10^13 Ω/sq is due to inserting an insulating buffer layer （two-step A1N buffer） between the high-temperature GaN layer and a sapphire substrate which blocks diffusion of oxygen and overcomes the weakness of generating high density carrier near interface of GaN and sapphire when a low-temperature GaN buffer is used. The result suggests that the high conductive feature of unintentionally doped GaN is mainly contributed from the highly conductive channel near interface between GaN and the sapphire substrate, which is indirectly manifested by room-temperature photoluminescence excited by an incident laser beam radiating on growth surface and on the substrate. The functions of the two-step A1N buffer layer in reducing screw dislocation and improving crystal quality of GaN are also discussed.