In this paper,large-sized sapphire (230×210 mm,27.5 kg) was grown by SAPMAC method (sapphire growth technique with micro-pulling and shoulder-expanding at the cooled center). Dislocation peculiarity in large sapphire boule (0001) basal plane was investigated by chemical etching,scanning electron microscopy and X-ray topography method. The triangular dislocation etch pit measured is 7.6×101~8.0×102 cm-2,in which relative high-density dislocations were generated at both initial and final stages of crystal growth. The analysis of single-crystal X-ray topography shows that there are no apparent sub-grain boundaries; the dislocation lines are isolated and straight. Finally,the origins of low-density dislocation in sapphire crystal are discussed by numerical analysis method. 相似文献
2.
冷心放肩微量提拉法大尺寸蓝宝石单晶生长过程的模拟分析 总被引:4,自引:1,他引:3
利用数值模拟方法计算了冷心放肩微量提拉法(SAPMAC)蓝宝石晶体生长过程.结合晶体直径变化、裂纹出现位置与延续方向、晶体透明性等实验现象,通过与提拉法、温梯法、坩埚移动法等相对比,分析了冷心放肩微量提拉法晶体生长各阶段的工艺特点,并根据模拟计算结果对晶体生长系统和晶体生长控制工艺进行了改进.分别利用增大热交换器的散热参数、降低加热温度、改进降温曲线、调节外加轴向和径向温度梯度的方式来实现对晶体生长的引晶、放肩、等径和收尾控制.通过实验比较证明了改进后的晶体生长系统和晶体生长控制工艺能够生长出性能较好的大尺寸蓝宝石晶体. 相似文献
3.
蓝宝石晶体热性能的各向异性对SAPMAC法晶体生长的影响 总被引:1,自引:1,他引:0
采用有限元法对冷心放肩微量提拉法蓝宝石晶体生长过程中晶体内的温度、应力分布进行了模拟计算,结合实验结果讨论了蓝宝石晶体热性能的各向异性对晶体生长的影响.研究结果表明,对于冷心放肩微量提拉蓝宝石晶体生长系统,较大的轴向热导率有利于提高晶体的生长速率和界面稳定性,而稍大的径向热导率则有利于保持微凸的生长界面.晶体内的热应力受径向热膨胀系数的影响显著,随着径向热膨胀系数的增大而增大,最大热应力总是出现在籽晶与新生晶体的界面区域.在实验中选α轴为结晶取向,成功生长出了直径达230mm、高质量蓝宝石晶体. 相似文献
4.
5.
6.
采用水平定向结晶法(HDS)成功生长出了质量优异的板状蓝宝石晶体.利用光学显微镜,扫描电镜(SEM),并结合化学腐蚀法对生长出的蓝宝石晶体不同位置的样品进行宏观缺陷及微观位错形貌的观测和研究,分析了水平定向结晶法生长蓝宝石晶体的宏观缺陷类型和位错的形貌,探讨了该缺陷在晶体中的分布规律及其形成原因.实验结果发现晶体的宏观缺陷主要包括气泡和包裹体.并结合能谱(EDS)测试包裹体的成分,分析其形成的原因.结果表明块状或絮状的小尺寸包裹体主要是由于C,Si杂质聚集原料中的其它杂质形成;长条形或圆形的大尺寸包裹体是由于Al,O元素的化学计量比严重适配,造成固液界面局部组分过冷形成.结合化学腐蚀法,发现该晶体的位错形貌均为三角型腐蚀坑,并探讨了晶体中位错的形态. 相似文献